Mapal Plastics Maplon CFA-HK Polypropylene Sheet
| Manufacturer | Mapal Plastics |
| Trade Name | Maplon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Applications: For use with electrical insulation products. For use when flame retardant and static dissipative properties are required.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc
@Thickness 0.430 mm
|
1.03 g/cc
@Thickness 0.0169 in
|
|
| 1.03 g/cc
@Thickness 0.250 mm
|
1.03 g/cc
@Thickness 0.00984 in
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 20.0 MPa
@Thickness 0.430 mm,
Temperature 23.0 °C |
2900 psi
@Thickness 0.0169 in,
Temperature 73.4 °F |
ASTM D638 |
| 20.0 MPa
@Thickness 0.250 mm,
Temperature 23.0 °C |
2900 psi
@Thickness 0.00984 in,
Temperature 73.4 °F |
ASTM D638 | |
| Film Tensile Strength at Yield, TD | 16.0 MPa
@Thickness 0.430 mm,
Temperature 23.0 °C |
2320 psi
@Thickness 0.0169 in,
Temperature 73.4 °F |
ASTM D638 |
| 16.0 MPa
@Thickness 0.250 mm,
Temperature 23.0 °C |
2320 psi
@Thickness 0.00984 in,
Temperature 73.4 °F |
ASTM D638 | |
| Film Elongation at Yield, MD | 16 %
@Thickness 0.250 mm,
Temperature 23.0 °C |
16 %
@Thickness 0.00984 in,
Temperature 73.4 °F |
ASTM D638 |
| 18 %
@Thickness 0.430 mm,
Temperature 23.0 °C |
18 %
@Thickness 0.0169 in,
Temperature 73.4 °F |
ASTM D638 | |
| Film Elongation at Yield, TD | 9.0 %
@Thickness 0.250 mm,
Temperature 23.0 °C |
9.0 %
@Thickness 0.00984 in,
Temperature 73.4 °F |
ASTM D638 |
| 14 %
@Thickness 0.430 mm,
Temperature 23.0 °C |
14 %
@Thickness 0.0169 in,
Temperature 73.4 °F |
ASTM D638 | |
| Modulus of Elasticity | 0.300 GPa
@Thickness 0.430 mm,
Temperature 23.0 °C |
43.5 ksi
@Thickness 0.0169 in,
Temperature 73.4 °F |
TD; ASTM D638 |
| 0.350 GPa
@Thickness 0.250 mm,
Temperature 23.0 °C |
50.8 ksi
@Thickness 0.00984 in,
Temperature 73.4 °F |
TD; ASTM D638 | |
| 0.350 GPa
@Thickness 0.430 mm,
Temperature 23.0 °C |
50.8 ksi
@Thickness 0.0169 in,
Temperature 73.4 °F |
ASTM D638 | |
| 0.400 GPa
@Thickness 0.250 mm,
Temperature 23.0 °C |
58.0 ksi
@Thickness 0.00984 in,
Temperature 73.4 °F |
ASTM D638 | |
| Flexural Modulus | 1.278 GPa
@Thickness 3.20 mm,
Temperature 23.0 °C |
185.4 ksi
@Thickness 0.126 in,
Temperature 73.4 °F |
|
| Izod Impact, Notched | 0.500 J/cm
@Thickness 3.20 mm,
Temperature -20.0 °C |
0.937 ft-lb/in
@Thickness 0.126 in,
Temperature -4.00 °F |
ASTM D256 |
| 2.50 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
4.68 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 150 °C
@Thickness 0.430 mm
|
302 °F
@Thickness 0.0169 in
|
ASTM D1525 |
| 150 °C
@Thickness 0.250 mm
|
302 °F
@Thickness 0.00984 in
|
ASTM D1525 | |
| Heat Distortion Temperature | 85.0 °C
@Thickness 0.430 mm
|
185 °F
@Thickness 0.0169 in
|
ASTM 648 |
| 85.0 °C
@Thickness 0.250 mm
|
185 °F
@Thickness 0.00984 in
|
ASTM 648 | |
| Flammability, UL94 | V-0
@Thickness 0.430 mm
|
V-0
@Thickness 0.0169 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 ohm
@Thickness 0.430 mm
|
1.00e+9 ohm
@Thickness 0.0169 in
|
ASTM D257 |
| 1.00e+9 ohm
@Thickness 0.250 mm
|
1.00e+9 ohm
@Thickness 0.00984 in
|
ASTM D257 | |
| Dielectric Breakdown | 15000 V
@Thickness 0.250 mm
|
15000 V
@Thickness 0.00984 in
|
ASTM D149 |
| 20000 V
@Thickness 0.430 mm
|
20000 V
@Thickness 0.0169 in
|
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |