Mapal Plastics Maplon Type D Polypropylene Sheet
| Manufacturer | Mapal Plastics |
| Trade Name | Maplon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Main advantages: High clarity and medium haze, High durability, Water and chemical resistance, High heat resistance, Unlimited flex life of integral hinge, Easy to convertMain disadvantages: Low scratch resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | |
| Thickness | 500 microns | 19.7 mil | |
| Surface Tension | >= 48 dynes/cm | >= 48 dynes/cm | After 2 months from production |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 30.0 MPa
@Temperature 23.0 °C
|
4350 psi
@Temperature 73.4 °F
|
ASTM D638 |
| Film Tensile Strength at Yield, TD | 29.0 MPa
@Temperature 23.0 °C
|
4210 psi
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Break, MD | >= 600 %
@Temperature 23.0 °C
|
>= 600 %
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Break, TD | >= 600 %
@Temperature 23.0 °C
|
>= 600 %
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Yield, MD | 24 %
@Temperature 23.0 °C
|
24 %
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Yield, TD | 23 %
@Temperature 23.0 °C
|
23 %
@Temperature 73.4 °F
|
ASTM D638 |
| Modulus of Elasticity | 0.280 GPa
@Temperature 23.0 °C
|
40.6 ksi
@Temperature 73.4 °F
|
MD/TD; ASTM D638 |
| Tear Strength | <= 130 kN/m | <= 742 pli | Mapal internal method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 136 °C | 277 °F | ASTM D1525 |
| Heat Distortion Temperature | 79.0 °C | 174 °F | ASTM D648 |