Mapal Plastics Maplon Type K OPAQLON COO1 Polypropylene Sheet
| Manufacturer | Mapal Plastics |
| Trade Name | Maplon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Maplon Catalog No. L050-C001K0101 is an extremely opaque white sheet. Sheet surface is smoothly embossed with similar finish on both sides..Main advantages: High opacity, High rigidity high thermal and chemical resistance, Good weather resistance, No yellowing after exposure to light, Good print-ability in all printing methods: offset UV and conventional, screen UV and solvent basedMain disadvantages: Due to sheet hardness it requires high pressure in die cutting, Material is not recommended for box production
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | |
| Thickness | 500 microns | 19.7 mil | |
| Surface Tension | >= 48 dynes/cm | >= 48 dynes/cm | Corona treated on both sides, After 2 months from production in original packaging |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ISO/R 868 |
| Film Tensile Strength at Yield, MD | 37.0 MPa
@Temperature 23.0 °C
|
5370 psi
@Temperature 73.4 °F
|
ASTM D638 |
| Film Tensile Strength at Yield, TD | 36.0 MPa
@Temperature 23.0 °C
|
5220 psi
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Break, MD | 50 %
@Temperature 23.0 °C
|
50 %
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Break, TD | 16 %
@Temperature 23.0 °C
|
16 %
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Yield, MD | 15 %
@Temperature 23.0 °C
|
15 %
@Temperature 73.4 °F
|
ASTM D638 |
| Film Elongation at Yield, TD | 12 %
@Temperature 23.0 °C
|
12 %
@Temperature 73.4 °F
|
ASTM D638 |
| Modulus of Elasticity | 0.570 GPa
@Temperature 23.0 °C
|
82.7 ksi
@Temperature 73.4 °F
|
MD/TD; ASTM D638 |
| Tear Strength | <= 230 kN/m | <= 1310 pli | Mapal internal |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 155 °C | 311 °F | ASTM D1525 |
| Heat Distortion Temperature | 110 °C | 230 °F | ASTM 648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | >= 99.5 % | >= 99.5 % | Measured in daylight |