Multibase Multi-Pro® 4003 RC 40% Glass Filled Polypropylene

Manufacturer Multibase
Trade Name Multi-Pro®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union

Description

Material Notes:
Multi-Pro 4003 RC is a chemically coupled glass reinforced polypropylene compound suitable for engineered plastics applications due to its high heat, flexural and impact properties.Data provided by Multibase.
Physical Properties Metric English Comments
Density 1.24 g/cc

0.0448 lb/in³

ASTM D792-91
Linear Mold Shrinkage 0.0030 cm/cm

0.0030 in/in

ASTM D955-89
Melt Flow 3.0 g/10 min

3.0 g/10 min

(Condition L) ASTM D-1238-94a

 

Mechanical Properties Metric English Comments
Hardness, Shore D 83

83

10 sec; ASTM D-2240-95
Tensile Strength, Ultimate 79.3 MPa

11500 psi

ASTM D638-95
Elongation at Break 3.0 %

3.0 %

ASTM D638-95
Flexural Strength 75.9 MPa

11000 psi

ASTM D790-95
Flexural Modulus 6.207 GPa

900.3 ksi

Method 1, Proc. B; ASTM D-790-95
Izod Impact, Notched 0.850 J/cm

1.59 ft-lb/in

ASTM D256-93a
Gardner Impact 0.300 J

0.221 ft-lb

ASTM D5420-93

 

Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 164 °C

327 °F

ASTM D648-95
Deflection Temperature at 1.8 MPa (264 psi) 149 °C

300 °F

ASTM D648-95