North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade
| Manufacturer | North Wood Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Data provided by North Wood Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.145 g/cc | 0.04137 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0018 cm/cm | 0.0018 in/in | ASTM D955 |
| Melt Flow | <= 0.50 g/10 min
@Temperature 190 °C
|
<= 0.50 g/10 min
@Temperature 374 °F
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D638 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ASTM D638 |
| Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 1% Secant at 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.0 µm/m-°C
@Temperature 20.0 °C
|
20.0 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 200 °C | <= 392 °F | To prevent fiber degradation. |