Overview of materials for Acrylic, Glass Fiber Reinforced
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Acrylic, Glass Fiber Reinforced”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 – 1.52 g/cc | 0.0455 – 0.0549 lb/in³ | Average value: 1.38 g/cc Grade Count:4 |
| Filler Content | 10.0 – 40.0 % | 10.0 – 40.0 % | Average value: 25.0 % Grade Count:4 |
| Water Absorption | 0.200 – 0.300 % | 0.200 – 0.300 % | Average value: 0.250 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00100 – 0.00400 cm/cm | 0.00100 – 0.00400 in/in | Average value: 0.00225 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 75.8 – 121 MPa | 11000 – 17500 psi | Average value: 97.4 MPa Grade Count:4 |
| Elongation at Break | 1.00 % | 1.00 % | Average value: 1.00 % Grade Count:4 |
| Modulus of Elasticity | 3.79 – 12.8 GPa | 550 – 1850 ksi | Average value: 8.45 GPa Grade Count:4 |
| Flexural Yield Strength | 110 – 179 MPa | 16000 – 26000 psi | Average value: 143 MPa Grade Count:4 |
| Flexural Modulus | 3.45 – 12.4 GPa | 500 – 1800 ksi | Average value: 8.27 GPa Grade Count:4 |
| Izod Impact, Notched | 0.427 – 0.534 J/cm | 0.800 – 1.00 ft-lb/in | Average value: 0.494 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 1.60 – 2.14 J/cm | 3.00 – 4.00 ft-lb/in | Average value: 1.80 J/cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 – 102 °C | 200 – 215 °F | Average value: 98.2 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 – 96.1 °C | 195 – 205 °F | Average value: 93.3 °C Grade Count:4 |
| Flammability, UL94 | HB | HB | Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 – 1.00e+17 ohm-cm | 1.00e+16 – 1.00e+17 ohm-cm | Average value: 7.75e+16 ohm-cm Grade Count:4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 177 – 210 °C | 350 – 410 °F | Average value: 193 °C Grade Count:4 |
| Mold Temperature | 79.4 – 107 °C | 175 – 225 °F | Average value: 93.3 °C Grade Count:4 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:4 |