Overview of materials for Acrylic, Heat Resistant, Molded
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Acrylic, Heat Resistant, Molded”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 – 1.19 g/cc | 0.0415 – 0.0430 lb/in³ | Average value: 1.18 g/cc Grade Count:17 |
| Water Absorption | 0.300 – 2.00 % | 0.300 – 2.00 % | Average value: 0.490 % Grade Count:10 |
| Water Absorption at Saturation | 0.300 % | 0.300 % | Average value: 0.300 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00200 – 0.00700 cm/cm | 0.00200 – 0.00700 in/in | Average value: 0.00423 cm/cm Grade Count:15 |
| Melt Flow | 0.900 – 19.0 g/10 min | 0.900 – 19.0 g/10 min | Average value: 3.77 g/10 min Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 44.0 – 105 | 44.0 – 105 | Average value: 85.7 Grade Count:14 |
| Tensile Strength, Ultimate | 44.1 – 80.0 MPa | 6400 – 11600 psi | Average value: 67.0 MPa Grade Count:14 |
| Tensile Strength, Yield | 71.7 – 76.0 MPa | 10400 – 11000 psi | Average value: 74.4 MPa Grade Count:3 |
| Elongation at Break | 3.00 – 30.0 % | 3.00 – 30.0 % | Average value: 11.8 % Grade Count:15 |
| Elongation at Yield | 4.00 – 13.0 % | 4.00 – 13.0 % | Average value: 6.14 % Grade Count:7 |
| Modulus of Elasticity | 1.72 – 3.60 GPa | 250 – 522 ksi | Average value: 2.86 GPa Grade Count:14 |
| Flexural Yield Strength | 68.9 – 133 MPa | 10000 – 19300 psi | Average value: 103 MPa Grade Count:15 |
| Flexural Modulus | 1.79 – 3.43 GPa | 260 – 498 ksi | Average value: 2.87 GPa Grade Count:14 |
| Izod Impact, Notched | 0.157 – 0.534 J/cm | 0.294 – 1.00 ft-lb/in | Average value: 0.280 J/cm Grade Count:13 |
| 0.240255 – 0.32034 J/cm
@Temperature 0.000 – 0.000 °C
|
0.450096 – 0.60013 ft-lb/in
@Temperature 32.0 – 32.0 °F
|
Average value: 0.274 J/cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 59.9 – 75.0 µm/m-°C | 33.3 – 41.7 µin/in-°F | Average value: 65.0 µm/m-°C Grade Count:3 |
| 72.0 – 90.0 µm/m-°C
@Temperature 0.000 – 156 °C
|
40.0 – 50.0 µin/in-°F
@Temperature 32.0 – 312 °F
|
Average value: 76.5 µm/m-°C Grade Count:4 | |
| Thermal Conductivity | 0.187 – 0.210 W/m-K | 1.30 – 1.46 BTU-in/hr-ft²-°F | Average value: 0.193 W/m-K Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.4 – 113 °C | 202 – 235 °F | Average value: 102 °C Grade Count:8 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 – 108 °C | 185 – 226 °F | Average value: 97.4 °C Grade Count:14 |
| Vicat Softening Point | 95.0 – 240 °C | 203 – 464 °F | Average value: 113 °C Grade Count:16 |
| Flammability, UL94 | HB | HB | Grade Count:8 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 – 1.51 | 1.49 – 1.51 | Average value: 1.49 Grade Count:12 |
| Haze | 0.300 – 96.0 % | 0.300 – 96.0 % | Average value: 8.90 % Grade Count:12 |
| Yellow Index | 0.300 – 5.50 % | 0.300 – 5.50 % | Average value: 1.60 % Grade Count:4 |
| Transmission, Visible | 80.0 – 93.0 % | 80.0 – 93.0 % | Average value: 90.9 % Grade Count:17 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.7 – 20.0 kV/mm | 475 – 508 kV/in | Average value: 19.6 kV/mm Grade Count:3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 250 °C | 428 – 482 °F | Average value: 240 °C Grade Count:5 |
| Mold Temperature | 43.3 – 90.0 °C | 110 – 194 °F | Average value: 65.2 °C Grade Count:5 |
| Drying Temperature | 82.2 – 109 °C | 180 – 228 °F | Average value: 87.6 °C Grade Count:5 |