Overview of materials for Acrylic, UV Stabilized, Molded
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Acrylic, UV Stabilized, Molded”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 – 1.20 g/cc | 0.0415 – 0.0434 lb/in³ | Average value: 1.18 g/cc Grade Count:14 |
| Water Absorption | 0.300 – 1.90 % | 0.300 – 1.90 % | Average value: 0.617 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00200 – 0.00800 cm/cm | 0.00200 – 0.00800 in/in | Average value: 0.00500 cm/cm Grade Count:8 |
| Melt Flow | 1.10 – 26.0 g/10 min | 1.10 – 26.0 g/10 min | Average value: 4.90 g/10 min Grade Count:13 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 20.0 – 94.0 | 20.0 – 94.0 | Average value: 67.7 Grade Count:7 |
| Tensile Strength, Ultimate | 32.4 – 70.3 MPa | 4700 – 10200 psi | Average value: 59.1 MPa Grade Count:13 |
| Elongation at Break | 2.00 – 50.0 % | 2.00 – 50.0 % | Average value: 13.8 % Grade Count:5 |
| Modulus of Elasticity | 1.79 – 3.45 GPa | 260 – 500 ksi | Average value: 2.77 GPa Grade Count:9 |
| Flexural Yield Strength | 55.2 – 117 MPa | 8000 – 17000 psi | Average value: 90.3 MPa Grade Count:8 |
| Flexural Modulus | 1.72 – 3.45 GPa | 250 – 500 ksi | Average value: 2.69 GPa Grade Count:8 |
| Izod Impact, Notched | 0.160 – 0.587 J/cm | 0.300 – 1.10 ft-lb/in | Average value: 0.322 J/cm Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 72.0 – 72.0 µm/m-°C
@Temperature 0.000 – 156 °C
|
40.0 – 40.0 µin/in-°F
@Temperature 32.0 – 312 °F
|
Average value: 72.0 µm/m-°C Grade Count:2 |
| Thermal Conductivity | 0.187 – 0.216 W/m-K | 1.30 – 1.50 BTU-in/hr-ft²-°F | Average value: 0.205 W/m-K Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 – 105 °C | 185 – 221 °F | Average value: 95.4 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 – 102 °C | 165 – 216 °F | Average value: 89.7 °C Grade Count:14 |
| Vicat Softening Point | 76.7 – 114 °C | 170 – 237 °F | Average value: 100 °C Grade Count:13 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | Average value: 1.49 Grade Count:5 |
| Haze | 1.00 – 3.00 % | 1.00 – 3.00 % | Average value: 2.25 % Grade Count:12 |
| Transmission, Visible | 80.0 – 92.0 % | 80.0 – 92.0 % | Average value: 90.3 % Grade Count:13 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 26.7 – 107 °C | 80.0 – 225 °F | Average value: 66.0 °C Grade Count:3 |