Overview of materials for PETG Copolyester
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “PETG Copolyester”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 – 1.33 g/cc | 0.0426 – 0.0480 lb/in³ | Average value: 1.27 g/cc Grade Count:20 |
| Water Absorption | 0.130 – 0.200 % | 0.130 – 0.200 % | Average value: 0.153 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 – 0.00600 cm/cm | 0.00200 – 0.00600 in/in | Average value: 0.00404 cm/cm Grade Count:12 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 – 119 | 105 – 119 | Average value: 110 Grade Count:7 |
| Tensile Strength, Ultimate | 26.0 – 57.9 MPa | 3770 – 8400 psi | Average value: 39.5 MPa Grade Count:17 |
| Tensile Strength, Yield | 28.3 – 58.6 MPa | 4100 – 8500 psi | Average value: 48.0 MPa Grade Count:10 |
| Elongation at Break | 5.00 – 350 % | 5.00 – 350 % | Average value: 104 % Grade Count:17 |
| Elongation at Yield | 3.90 – 4.10 % | 3.90 – 4.10 % | Average value: 4.00 % Grade Count:5 |
| Modulus of Elasticity | 1.10 – 2.69 GPa | 160 – 390 ksi | Average value: 1.93 GPa Grade Count:16 |
| Flexural Yield Strength | 39.2 – 88.9 MPa | 5690 – 12900 psi | Average value: 72.0 MPa Grade Count:16 |
| Flexural Modulus | 1.24 – 2.76 GPa | 180 – 400 ksi | Average value: 1.99 GPa Grade Count:18 |
| Izod Impact, Notched | 0.267 – 10.7 J/cm | 0.500 – 20.0 ft-lb/in | Average value: 3.01 J/cm Grade Count:13 |
| 0.270 – 0.520 J/cm
@Temperature -40.0 – -40.0 °C
|
0.506 – 0.974 ft-lb/in
@Temperature -40.0 – -40.0 °F
|
Average value: 0.360 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 0.497 – 13.3 J/cm | 0.930 – 25.0 ft-lb/in | Average value: 6.94 J/cm Grade Count:7 |
| 0.277628 – 0.277628 J/cm
@Temperature -40.0 – -40.0 °C
|
0.520111 – 0.520111 ft-lb/in
@Temperature -40.0 – -40.0 °F
|
Average value: 0.278 J/cm Grade Count:1 | |
| Charpy Impact Unnotched | NB – NB
@Temperature -30.0 – -30.0 °C
|
NB – NB
@Temperature -22.0 – -22.0 °F
|
Grade Count:2 |
| Charpy Impact, Notched | 0.310 – 0.370 J/cm²
@Temperature -30.0 – -30.0 °C
|
1.48 – 1.76 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 0.340 J/cm² Grade Count:2 |
| Falling Dart Impact | 542.328 – 542.328 J
@Temperature -40.0 – -40.0 °C
|
400.001 – 400.001 ft-lb
@Temperature -40.0 – -40.0 °F
|
Average value: 542 J Grade Count:1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.0 – 100 µm/m-°C | 23.9 – 55.6 µin/in-°F | Average value: 67.8 µm/m-°C Grade Count:5 |
| Thermal Conductivity | 0.190 – 0.225 W/m-K | 1.32 – 1.56 BTU-in/hr-ft²-°F | Average value: 0.202 W/m-K Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 – 98.9 °C | 140 – 210 °F | Average value: 70.6 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 – 90.0 °C | 131 – 194 °F | Average value: 65.1 °C Grade Count:13 |
| Vicat Softening Point | 73.0 – 85.0 °C | 163 – 185 °F | Average value: 79.2 °C Grade Count:5 |
| Glass Transition Temp, Tg | 79.0 – 81.1 °C | 174 – 178 °F | Average value: 80.0 °C Grade Count:5 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.300 – 1.00 % | 0.300 – 1.00 % | Average value: 0.680 % Grade Count:5 |
| Transmission, Visible | 82.0 – 91.0 % | 82.0 – 91.0 % | Average value: 88.0 % Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10.0 – 1.00e+15 ohm-cm | 10.0 – 1.00e+15 ohm-cm | Average value: 1.67e+14 ohm-cm Grade Count:12 |
| Surface Resistance | 1000 – 1.00e+16 ohm | 1000 – 1.00e+16 ohm | Average value: 7.69e+14 ohm Grade Count:9 |
| Static Decay | 0.0100 – 2.00 sec | 0.0100 – 2.00 sec | Average value: 1.03 sec Grade Count:7 |
| Dielectric Constant | 2.40 – 2.60 | 2.40 – 2.60 | Average value: 2.50 Grade Count:3 |
| Dielectric Strength | 16.0 – 16.1 kV/mm | 406 – 410 kV/in | Average value: 16.1 kV/mm Grade Count:3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 45.0 – 249 °C | 113 – 480 °F | Average value: 171 °C Grade Count:5 |
| Die Temperature | 195 – 293 °C | 383 – 560 °F | Average value: 254 °C Grade Count:5 |
| Melt Temperature | 180 – 293 °C | 356 – 560 °F | Average value: 245 °C Grade Count:9 |
| Mold Temperature | 12.0 – 70.0 °C | 53.6 – 158 °F | Average value: 31.9 °C Grade Count:4 |
| Drying Temperature | 65.0 – 102 °C | 149 – 216 °F | Average value: 71.5 °C Grade Count:7 |
| Moisture Content | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:4 |
| Dew Point | -33.9 °C | -29.0 °F | Average value: -33.9 °C Grade Count:4 |