Overview of materials for Polycarbonate/Polysulfone Alloy
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polycarbonate/Polysulfone Alloy”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 – 1.53 g/cc | 0.0441 – 0.0553 lb/in³ | Average value: 1.35 g/cc Grade Count:7 |
| Filler Content | 10.0 – 20.0 % | 10.0 – 20.0 % | Average value: 16.7 % Grade Count:3 |
| Water Absorption | 0.180 – 0.200 % | 0.180 – 0.200 % | Average value: 0.193 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00150 – 0.0100 cm/cm | 0.00150 – 0.0100 in/in | Average value: 0.00450 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 65.5 – 138 MPa | 9500 – 20000 psi | Average value: 95.2 MPa Grade Count:7 |
| Elongation at Break | 1.50 – 100 % | 1.50 – 100 % | Average value: 18.4 % Grade Count:7 |
| Modulus of Elasticity | 2.34 – 11.0 GPa | 340 – 1600 ksi | Average value: 5.60 GPa Grade Count:7 |
| Flexural Yield Strength | 93.1 – 207 MPa | 13500 – 30000 psi | Average value: 142 MPa Grade Count:7 |
| Flexural Modulus | 2.62 – 10.7 GPa | 380 – 1550 ksi | Average value: 5.33 GPa Grade Count:7 |
| Izod Impact, Notched | 0.534 – 1.07 J/cm | 1.00 – 2.00 ft-lb/in | Average value: 0.839 J/cm Grade Count:7 |
| Izod Impact, Unnotched | 3.20 – 5340 J/cm | 6.00 – 10000 ft-lb/in | Average value: 8.10 J/cm Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 149 – 163 °C | 300 – 325 °F | Average value: 154 °C Grade Count:7 |
| Flammability, UL94 | V-2 – V-0 | V-2 – V-0 | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 – 327 °C | 540 – 620 °F | Average value: 304 °C Grade Count:5 |
| Mold Temperature | 65.6 – 98.9 °C | 150 – 210 °F | Average value: 82.2 °C Grade Count:7 |
| Drying Temperature | 121 °C | 250 °F | Average value: 121 °C Grade Count:5 |
| Moisture Content | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:5 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:5 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:7 |