This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Flame Retardant”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.850 – 1.90 g/cc | 0.0307 – 0.0686 lb/in³ | Average value: 1.09 g/cc Grade Count:250 |
| Filler Content | 10.0 – 40.0 % | 10.0 – 40.0 % | Average value: 23.7 % Grade Count:18 |
| Water Absorption | 0.0100 – 0.0500 % | 0.0100 – 0.0500 % | Average value: 0.0227 % Grade Count:49 |
| Maximum Moisture Content | 0.0100 – 0.0200 | 0.0100 – 0.0200 | Average value: 0.0125 Grade Count:4 |
| Linear Mold Shrinkage | 0.000100 – 0.0500 cm/cm | 0.000100 – 0.0500 in/in | Average value: 0.0144 cm/cm Grade Count:176 |
| Linear Mold Shrinkage, Transverse | 0.00700 – 0.0243 cm/cm | 0.00700 – 0.0243 in/in | Average value: 0.0164 cm/cm Grade Count:29 |
| Melt Flow | 0.300 – 140 g/10 min | 0.300 – 140 g/10 min | Average value: 12.4 g/10 min Grade Count:170 |
| Ash | 15.0 – 25.0 % | 15.0 – 25.0 % | Average value: 20.0 % Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | Average value: 100 Grade Count:4 |
| Hardness, Rockwell R | 69.0 – 105 | 69.0 – 105 | Average value: 89.7 Grade Count:20 |
| Hardness, Shore A | 66.0 – 69.0 | 66.0 – 69.0 | Average value: 67.8 Grade Count:6 |
| Hardness, Shore D | 60.0 – 80.0 | 60.0 – 80.0 | Average value: 71.0 Grade Count:30 |
| Tensile Strength, Ultimate | 10.3 – 300 MPa | 1500 – 43500 psi | Average value: 31.7 MPa Grade Count:167 |
| 7.00 – 45.0 MPa
@Temperature 60.0 – 90.0 °C
|
1020 – 6530 psi
@Temperature 140 – 194 °F
|
Average value: 16.9 MPa Grade Count:4 | |
| Tensile Strength, Yield | 2.07 – 75.0 MPa | 300 – 10900 psi | Average value: 27.9 MPa Grade Count:100 |
| Elongation at Break | 1.00 – 558 % | 1.00 – 558 % | Average value: 64.0 % Grade Count:182 |
| 4.00 – 20.0 %
@Temperature 60.0 – 90.0 °C
|
4.00 – 20.0 %
@Temperature 140 – 194 °F
|
Average value: 66.2 % Grade Count:8 | |
| Elongation at Yield | 2.00 – 350 % | 2.00 – 350 % | Average value: 31.6 % Grade Count:46 |
| 2.50 – 10.0 %
@Temperature 60.0 – 90.0 °C
|
2.50 – 10.0 %
@Temperature 140 – 194 °F
|
Average value: 7.56 % Grade Count:8 | |
| Modulus of Elasticity | 0.800 – 9.31 GPa | 116 – 1350 ksi | Average value: 2.08 GPa Grade Count:120 |
| 0.300 – 5.70 GPa
@Temperature 60.0 – 90.0 °C
|
43.5 – 827 ksi
@Temperature 140 – 194 °F
|
Average value: 1.26 GPa Grade Count:8 | |
| Flexural Yield Strength | 17.9 – 300 MPa | 2600 – 43500 psi | Average value: 40.5 MPa Grade Count:128 |
| Flexural Modulus | 0.621 – 7.24 GPa | 90.0 – 1050 ksi | Average value: 1.79 GPa Grade Count:199 |
| Izod Impact, Notched | 0.107 J/cm – NB | 0.200 ft-lb/in – NB | Average value: 0.913 J/cm Grade Count:165 |
| 0.150 – 0.550 J/cm
@Temperature -20.0 – 0.000 °C
|
0.281 – 1.03 ft-lb/in
@Temperature -4.00 – 32.0 °F
|
Average value: 0.329 J/cm Grade Count:17 | |
| Izod Impact, Unnotched | 0.801 – 5340 J/cm | 1.50 – 10000 ft-lb/in | Average value: 8.47 J/cm Grade Count:46 |
| Izod Impact, Notched (ISO) | 2.00 – 60.0 kJ/m² | 0.952 – 28.6 ft-lb/in² | Average value: 7.59 kJ/m² Grade Count:44 |
| 2.00 – 10.0 kJ/m²
@Temperature -30.0 – -20.0 °C
|
0.952 – 4.76 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 4.11 kJ/m² Grade Count:9 | |
| Izod Impact, Unnotched (ISO) | 15.0 – 98.0 kJ/m² | 7.14 – 46.6 ft-lb/in² | Average value: 56.2 kJ/m² Grade Count:10 |
| 13.0 – 13.0 kJ/m²
@Temperature -30.0 – -30.0 °C
|
6.19 – 6.19 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 13.0 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 1.00 J/cm² – NB | 4.76 ft-lb/in² – NB | Average value: 4.21 J/cm² Grade Count:48 |
| 0.650 – 999.9 J/cm²
@Temperature -40.0 – -20.0 °C
|
3.09 – 4759 ft-lb/in²
@Temperature -40.0 – -4.00 °F
|
Average value: 3.16 J/cm² Grade Count:26 | |
| Charpy Impact, Notched | 0.150 – 9.00 J/cm² | 0.714 – 42.8 ft-lb/in² | Average value: 0.657 J/cm² Grade Count:53 |
| 0.0400 – 1.40 J/cm²
@Temperature -30.0 – -20.0 °C
|
0.190 – 6.66 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 0.266 J/cm² Grade Count:30 | |
| Gardner Impact | 0.904 – 260 J | 0.667 – 192 ft-lb | Average value: 26.8 J Grade Count:24 |
| Dart Drop, Total Energy | 2.71 – 14.9 J | 2.00 – 11.0 ft-lb | Average value: 8.59 J Grade Count:3 |
| Dart Drop Total Energy | 1.44 – 8.54 J/cm | 0.00270 – 0.0160 ft-lb/mil | Average value: 6.10 J/cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 – 120 µm/m-°C | 17.2 – 66.7 µin/in-°F | Average value: 69.8 µm/m-°C Grade Count:10 |
| CTE, linear, Transverse to Flow | 96.0 – 140 µm/m-°C | 53.3 – 77.8 µin/in-°F | Average value: 116 µm/m-°C Grade Count:4 |
| Thermal Conductivity | 0.170 – 0.303 W/m-K | 1.18 – 2.10 BTU-in/hr-ft²-°F | Average value: 0.258 W/m-K Grade Count:3 |
| Melting Point | 130 – 170 °C | 266 – 338 °F | Average value: 162 °C Grade Count:52 |
| Maximum Service Temperature, Air | 60.0 – 130 °C | 140 – 266 °F | Average value: 92.7 °C Grade Count:14 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 – 187 °C | 158 – 368 °F | Average value: 109 °C Grade Count:119 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.6 – 155 °C | 105 – 311 °F | Average value: 68.4 °C Grade Count:152 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10.0 – 1.00e+17 ohm-cm | 10.0 – 1.00e+17 ohm-cm | Average value: 4.60e+15 ohm-cm Grade Count:80 |
| Surface Resistance | 1000 – 1.00e+16 ohm | 1000 – 1.00e+16 ohm | Average value: 2.31e+15 ohm Grade Count:45 |
| Static Decay | 0.500 – 2.00 sec | 0.500 – 2.00 sec | Average value: 1.50 sec Grade Count:3 |
| Dielectric Constant | 2.10 – 3.06 | 2.10 – 3.06 | Average value: 2.50 Grade Count:9 |
| Dielectric Strength | 17.7 – 43.0 kV/mm | 450 – 1090 kV/in | Average value: 28.8 kV/mm Grade Count:50 |
| Dissipation Factor | 0.00120 – 0.0100 | 0.00120 – 0.0100 | Average value: 0.00380 Grade Count:4 |
| Arc Resistance | 60.0 – 180 sec | 60.0 – 180 sec | Average value: 124 sec Grade Count:6 |
| Comparative Tracking Index | 350 – 600 V | 350 – 600 V | Average value: 552 V Grade Count:52 |
| Hot Wire Ignition, HWI | 7.00 – 60.0 sec | 7.00 – 60.0 sec | Average value: 26.8 sec Grade Count:4 |
| High Amp Arc Ignition, HAI | 120 arcs | 120 arcs | Average value: 120 arcs Grade Count:4 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 – 330 mm/min | 0.000 – 13.0 in/min | Average value: 116 mm/min Grade Count:3 |