This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Long Glass Fiber 50%”. Specific grades with glass content between 45% and 54% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 – 1.68 g/cc | 0.0379 – 0.0607 lb/in³ | Average value: 1.31 g/cc Grade Count:46 |
| Filler Content | 45.0 – 50.0 % | 45.0 – 50.0 % | Average value: 48.6 % Grade Count:9 |
| Water Absorption | 0.0100 – 0.0600 % | 0.0100 – 0.0600 % | Average value: 0.0517 % Grade Count:6 |
| Linear Mold Shrinkage | 0.000300 – 0.00780 cm/cm | 0.000300 – 0.00780 in/in | Average value: 0.00304 cm/cm Grade Count:17 |
| Linear Mold Shrinkage, Transverse | 0.00750 – 0.0128 cm/cm | 0.00750 – 0.0128 in/in | Average value: 0.0113 cm/cm Grade Count:3 |
| Melt Flow | 2.50 – 10.0 g/10 min | 2.50 – 10.0 g/10 min | Average value: 5.43 g/10 min Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 – 112 | 110 – 112 | Average value: 111 Grade Count:3 |
| Tensile Strength, Ultimate | 49.6 – 400 MPa | 7200 – 58000 psi | Average value: 132 MPa Grade Count:34 |
| 40.0 – 85.0 MPa
@Temperature 60.0 – 90.0 °C
|
5800 – 12300 psi
@Temperature 140 – 194 °F
|
Average value: 78.1 MPa Grade Count:12 | |
| Tensile Strength, Yield | 60.0 – 135 MPa | 8700 – 19600 psi | Average value: 115 MPa Grade Count:12 |
| Elongation at Break | 1.00 – 4.00 % | 1.00 – 4.00 % | Average value: 1.98 % Grade Count:42 |
| 2.20 – 5.80 %
@Temperature 60.0 – 90.0 °C
|
2.20 – 5.80 %
@Temperature 140 – 194 °F
|
Average value: 2.65 % Grade Count:12 | |
| Elongation at Yield | 2.00 – 4.00 % | 2.00 – 4.00 % | Average value: 3.00 % Grade Count:3 |
| 2.70 – 4.20 %
@Temperature 60.0 – 90.0 °C
|
2.70 – 4.20 %
@Temperature 140 – 194 °F
|
Average value: 3.45 % Grade Count:1 | |
| Modulus of Elasticity | 6.85 – 20.5 GPa | 994 – 2970 ksi | Average value: 11.5 GPa Grade Count:40 |
| 5.30 – 8.40 GPa
@Temperature 60.0 – 90.0 °C
|
769 – 1220 ksi
@Temperature 140 – 194 °F
|
Average value: 7.70 GPa Grade Count:12 | |
| Flexural Yield Strength | 62.1 – 370 MPa | 9000 – 53700 psi | Average value: 188 MPa Grade Count:43 |
| 90.0 – 130 MPa
@Temperature 80.0 – 80.0 °C
|
13100 – 18900 psi
@Temperature 176 – 176 °F
|
Average value: 121 MPa Grade Count:9 | |
| Flexural Modulus | 3.86 – 17.5 GPa | 560 – 2540 ksi | Average value: 10.1 GPa Grade Count:44 |
| 6.00 – 9.00 GPa
@Temperature 80.0 – 80.0 °C
|
870 – 1310 ksi
@Temperature 176 – 176 °F
|
Average value: 7.78 GPa Grade Count:9 | |
| Izod Impact, Notched | 0.534 – 3.50 J/cm | 1.00 – 6.56 ft-lb/in | Average value: 2.10 J/cm Grade Count:24 |
| 1.10 – 1.30 J/cm
@Temperature -20.0 – 0.000 °C
|
2.06 – 2.44 ft-lb/in
@Temperature -4.00 – 32.0 °F
|
Average value: 1.20 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.60 – 9.61 J/cm | 3.00 – 18.0 ft-lb/in | Average value: 6.63 J/cm Grade Count:11 |
| Izod Impact, Notched (ISO) | 20.0 – 25.0 kJ/m² | 9.52 – 11.9 ft-lb/in² | Average value: 23.3 kJ/m² Grade Count:3 |
| 15.0 – 15.0 kJ/m²
@Temperature -30.0 – -30.0 °C
|
7.14 – 7.14 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 15.0 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 2.00 – 8.00 J/cm² | 9.52 – 38.1 ft-lb/in² | Average value: 6.12 J/cm² Grade Count:16 |
| 1.80 – 8.20 J/cm²
@Temperature -30.0 – -20.0 °C
|
8.57 – 39.0 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 5.75 J/cm² Grade Count:14 | |
| Charpy Impact, Notched | 0.500 – 4.40 J/cm² | 2.38 – 20.9 ft-lb/in² | Average value: 2.52 J/cm² Grade Count:23 |
| 0.400 – 4.00 J/cm²
@Temperature -30.0 – -20.0 °C
|
1.90 – 19.0 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 2.71 J/cm² Grade Count:14 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 – 28.8 µm/m-°C | 12.0 – 16.0 µin/in-°F | Average value: 24.0 µm/m-°C Grade Count:3 |
| Melting Point | 160 – 167 °C | 320 – 333 °F | Average value: 164 °C Grade Count:18 |
| Maximum Service Temperature, Air | 90.0 – 140 °C | 194 – 284 °F | Average value: 116 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 – 163 °C | 300 – 325 °F | Average value: 158 °C Grade Count:9 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 – 165 °C | 250 – 329 °F | Average value: 153 °C Grade Count:41 |
| Deflection Temperature at 8.0 MPa | 132 – 138 °C | 270 – 280 °F | Average value: 136 °C Grade Count:10 |
| Vicat Softening Point | 140 – 163 °C | 284 – 325 °F | Average value: 151 °C Grade Count:4 |
| Flammability, UL94 | HB | HB | Grade Count:14 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 – 2.00e+16 ohm-cm | 1.00e+15 – 2.00e+16 ohm-cm | Average value: 7.33e+15 ohm-cm Grade Count:6 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 30.0 – 290 °C | 86.0 – 554 °F | Average value: 137 °C Grade Count:24 |
| Nozzle Temperature | 204 – 249 °C | 400 – 480 °F | Average value: 225 °C Grade Count:3 |
| Die Temperature | 225 – 290 °C | 437 – 554 °F | Average value: 265 °C Grade Count:18 |
| Melt Temperature | 191 – 290 °C | 375 – 554 °F | Average value: 249 °C Grade Count:27 |
| Mold Temperature | 20.0 – 80.0 °C | 68.0 – 176 °F | Average value: 56.0 °C Grade Count:18 |
| Injection Velocity | 50.0 – 80.0 mm/sec | 1.97 – 3.15 in/sec | Average value: 64.5 mm/sec Grade Count:3 |
| Drying Temperature | 79.4 – 100 °C | 175 – 212 °F | Average value: 92.3 °C Grade Count:22 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:18 |
| Injection Pressure | 60.0 – 120 MPa | 8700 – 17400 psi | Average value: 88.2 MPa Grade Count:21 |
| Hot-Working Temperature | 260 – 290 °C | 500 – 554 °F | Average value: 275 °C Grade Count:4 |