Overview of materials for Polypropylene, Mineral Reinforced, Impact Modified
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Mineral Reinforced, Impact Modified”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 – 1.34 g/cc | 0.0347 – 0.0484 lb/in³ | Average value: 1.07 g/cc Grade Count:42 |
| Maximum Moisture Content | 0.0100 | 0.0100 | Average value: 0.0100 Grade Count:26 |
| Linear Mold Shrinkage | 0.00200 – 0.0400 cm/cm | 0.00200 – 0.0400 in/in | Average value: 0.0108 cm/cm Grade Count:35 |
| Linear Mold Shrinkage, Transverse | 0.00700 – 0.0120 cm/cm | 0.00700 – 0.0120 in/in | Average value: 0.00995 cm/cm Grade Count:4 |
| Melt Flow | 3.00 – 40.0 g/10 min | 3.00 – 40.0 g/10 min | Average value: 15.9 g/10 min Grade Count:36 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 69.0 – 90.0 | 69.0 – 90.0 | Average value: 86.0 Grade Count:7 |
| Tensile Strength, Ultimate | 14.0 – 26.0 MPa | 2030 – 3770 psi | Average value: 18.9 MPa Grade Count:11 |
| Tensile Strength, Yield | 14.7 – 65.8 MPa | 2130 – 9550 psi | Average value: 25.0 MPa Grade Count:31 |
| Elongation at Break | 4.00 – 300 % | 4.00 – 300 % | Average value: 85.9 % Grade Count:39 |
| Modulus of Elasticity | 1.10 – 2.40 GPa | 160 – 348 ksi | Average value: 1.78 GPa Grade Count:4 |
| Flexural Yield Strength | 15.7 – 97.2 MPa | 2280 – 14100 psi | Average value: 35.2 MPa Grade Count:37 |
| Flexural Modulus | 1.02 – 4.55 GPa | 148 – 660 ksi | Average value: 2.03 GPa Grade Count:39 |
| Izod Impact, Notched | 0.430 – 4.90 J/cm | 0.806 – 9.19 ft-lb/in | Average value: 2.11 J/cm Grade Count:36 |
| >= 0.343233 J/cm
@Temperature -30.0 – -10.0 °C
|
>= 0.643016 ft-lb/in
@Temperature -22.0 – 14.0 °F
|
Average value: 0.537 J/cm Grade Count:17 | |
| >= 0.343233 J/cm
@Thickness 6.40 – 6.40 mm
|
>= 0.643016 ft-lb/in
@Thickness 0.252 – 0.252 in
|
Average value: 0.537 J/cm Grade Count:17 | |
| Izod Impact, Unnotched | 2.08 J/cm – NB | 3.90 ft-lb/in – NB | Average value: 5.69 J/cm Grade Count:7 |
| Charpy Impact Unnotched | 3.80 – 1000 J/cm² | 18.1 – 4760 ft-lb/in² | Average value: 4.90 J/cm² Grade Count:6 |
| 1.40 – 999.9 J/cm²
@Temperature -40.0 – -20.0 °C
|
6.66 – 4759 ft-lb/in²
@Temperature -40.0 – -4.00 °F
|
Average value: 1.40 J/cm² Grade Count:3 | |
| Charpy Impact, Notched | 0.300 – 7.50 J/cm² | 1.43 – 35.7 ft-lb/in² | Average value: 2.89 J/cm² Grade Count:5 |
| 2.00 – 4.80 J/cm²
@Temperature -20.0 – -20.0 °C
|
9.52 – 22.8 ft-lb/in²
@Temperature -4.00 – -4.00 °F
|
Average value: 3.40 J/cm² Grade Count:2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 – 145 °C | 169 – 293 °F | Average value: 117 °C Grade Count:35 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 – 146 °C | 124 – 295 °F | Average value: 69.8 °C Grade Count:13 |
| Vicat Softening Point | 100 – 140 °C | 212 – 284 °F | Average value: 120 °C Grade Count:4 |
| Flammability, UL94 | HB – V-0 | HB – V-0 | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 210 – 230 °C | 410 – 446 °F | Average value: 220 °C Grade Count:26 |
| Melt Temperature | 190 – 250 °C | 374 – 482 °F | Average value: 212 °C Grade Count:31 |
| Mold Temperature | 40.0 – 70.0 °C | 104 – 158 °F | Average value: 50.7 °C Grade Count:30 |
| Drying Temperature | 70.0 – 80.0 °C | 158 – 176 °F | Average value: 75.4 °C Grade Count:28 |