Overview of materials for Polypropylene with 10% Mica Filler
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene with 10% Mica Filler”. Specific grades with primary filler content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 – 1.01 g/cc | 0.0343 – 0.0365 lb/in³ | Average value: 0.967 g/cc Grade Count:14 |
| Filler Content | 12.0 % | 12.0 % | Average value: 12.0 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00800 – 0.0160 cm/cm | 0.00800 – 0.0160 in/in | Average value: 0.0109 cm/cm Grade Count:14 |
| Melt Flow | 3.00 – 20.0 g/10 min | 3.00 – 20.0 g/10 min | Average value: 12.8 g/10 min Grade Count:13 |
| Ash | 10.0 % | 10.0 % | Average value: 10.0 % Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 51.0 – 95.0 | 51.0 – 95.0 | Average value: 78.2 Grade Count:10 |
| Hardness, Shore D | 69.0 – 75.0 | 69.0 – 75.0 | Average value: 71.0 Grade Count:3 |
| Tensile Strength, Ultimate | 13.0 – 35.0 MPa | 1890 – 5080 psi | Average value: 23.9 MPa Grade Count:12 |
| Tensile Strength, Yield | 17.0 – 37.0 MPa | 2470 – 5370 psi | Average value: 29.8 MPa Grade Count:12 |
| Elongation at Break | 17.0 – 27.0 % | 17.0 – 27.0 % | Average value: 21.2 % Grade Count:10 |
| Elongation at Yield | 5.00 – 8.00 % | 5.00 – 8.00 % | Average value: 6.20 % Grade Count:10 |
| Modulus of Elasticity | 1.10 – 1.90 GPa | 160 – 276 ksi | Average value: 1.64 GPa Grade Count:9 |
| Flexural Yield Strength | 21.0 – 48.0 MPa | 3050 – 6960 psi | Average value: 36.6 MPa Grade Count:10 |
| Flexural Modulus | 1.10 – 6.40 GPa | 160 – 928 ksi | Average value: 2.01 GPa Grade Count:15 |
| Izod Impact, Notched | 0.320 – 2.99 J/cm | 0.600 – 5.60 ft-lb/in | Average value: 0.842 J/cm Grade Count:15 |
| Gardner Impact | 0.339 – 4.07 J | 0.250 – 3.00 ft-lb | Average value: 2.82 J Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 74.4 – 121 °C | 166 – 250 °F | Average value: 100 °C Grade Count:15 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 – 65.6 °C | 120 – 150 °F | Average value: 58.3 °C Grade Count:14 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 210 – 221 °C | 410 – 430 °F | Average value: 216 °C Grade Count:3 |
| Melt Temperature | 193 – 232 °C | 380 – 450 °F | Average value: 213 °C Grade Count:3 |
| Mold Temperature | 26.7 – 48.9 °C | 80.0 – 120 °F | Average value: 37.8 °C Grade Count:3 |
| Drying Temperature | 65.6 – 82.2 °C | 150 – 180 °F | Average value: 73.9 °C Grade Count:3 |
| Moisture Content | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:3 |
| Injection Pressure | 2.76 – 10.3 MPa | 400 – 1500 psi | Average value: 6.55 MPa Grade Count:3 |