Overview of materials for Polypropylene, Wood Filled
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Wood Filled”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 – 1.21 g/cc | 0.0344 – 0.0437 lb/in³ | Average value: 1.03 g/cc Grade Count:22 |
| Linear Mold Shrinkage | 0.00180 – 0.0100 cm/cm | 0.00180 – 0.0100 in/in | Average value: 0.00549 cm/cm Grade Count:14 |
| Melt Flow | 0.500 – 7.40 g/10 min | 0.500 – 7.40 g/10 min | Average value: 2.65 g/10 min Grade Count:12 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.0 – 62.1 MPa | 2900 – 9000 psi | Average value: 36.6 MPa Grade Count:16 |
| Tensile Strength, Yield | 21.0 – 40.0 MPa | 3050 – 5800 psi | Average value: 28.4 MPa Grade Count:9 |
| Elongation at Break | 1.20 – 10.0 % | 1.20 – 10.0 % | Average value: 5.18 % Grade Count:20 |
| Modulus of Elasticity | 1.72 – 6.20 GPa | 250 – 899 ksi | Average value: 3.26 GPa Grade Count:20 |
| Flexural Yield Strength | 38.0 – 103 MPa | 5510 – 15000 psi | Average value: 57.6 MPa Grade Count:19 |
| Flexural Modulus | 1.79 – 4.90 GPa | 260 – 711 ksi | Average value: 2.96 GPa Grade Count:21 |
| Izod Impact, Notched | 0.220 – 0.801 J/cm | 0.412 – 1.50 ft-lb/in | Average value: 0.471 J/cm Grade Count:18 |
| Izod Impact, Unnotched | 0.400 – 5.34 J/cm | 0.749 – 10.0 ft-lb/in | Average value: 3.00 J/cm Grade Count:18 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.0 – 63.0 µm/m-°C | 20.0 – 35.0 µin/in-°F | Average value: 49.7 µm/m-°C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.6 – 142 °C | 150 – 288 °F | Average value: 122 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 – 128 °C | 140 – 262 °F | Average value: 78.0 °C Grade Count:18 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | Average value: 200 °C Grade Count:8 |
| Melt Temperature | 185 – 232 °C | 365 – 450 °F | Average value: 203 °C Grade Count:13 |
| Mold Temperature | 30.0 – 65.6 °C | 86.0 – 150 °F | Average value: 47.4 °C Grade Count:12 |
| Drying Temperature | 70.0 – 90.0 °C | 158 – 194 °F | Average value: 78.4 °C Grade Count:13 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:10 |