Overview of materials for Polysulfone, 10% Glass Fiber Reinforced
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polysulfone, 10% Glass Fiber Reinforced”. Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 – 1.49 g/cc | 0.0459 – 0.0538 lb/in³ | Average value: 1.34 g/cc Grade Count:14 |
| Filler Content | 5.00 – 10.0 % | 5.00 – 10.0 % | Average value: 9.38 % Grade Count:8 |
| Water Absorption | 0.210 – 0.230 % | 0.210 – 0.230 % | Average value: 0.223 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 – 0.00700 cm/cm | 0.00200 – 0.00700 in/in | Average value: 0.00429 cm/cm Grade Count:14 |
| Melt Flow | 6.50 g/10 min | 6.50 g/10 min | Average value: 6.50 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 – 123 | 122 – 123 | Average value: 122 Grade Count:7 |
| Tensile Strength, Ultimate | 68.9 – 108 MPa | 10000 – 15700 psi | Average value: 82.2 MPa Grade Count:13 |
| Elongation at Break | 2.00 – 8.00 % | 2.00 – 8.00 % | Average value: 4.50 % Grade Count:14 |
| Modulus of Elasticity | 3.03 – 8.69 GPa | 440 – 1260 ksi | Average value: 4.49 GPa Grade Count:13 |
| Flexural Yield Strength | 110 – 154 MPa | 16000 – 22300 psi | Average value: 129 MPa Grade Count:14 |
| Flexural Modulus | 3.17 – 7.58 GPa | 460 – 1100 ksi | Average value: 4.24 GPa Grade Count:14 |
| Izod Impact, Notched | 0.267 – 0.801 J/cm | 0.500 – 1.50 ft-lb/in | Average value: 0.617 J/cm Grade Count:14 |
| Izod Impact, Unnotched | 3.74 – 13.3 J/cm | 7.00 – 25.0 ft-lb/in | Average value: 6.86 J/cm Grade Count:10 |
| Tensile Impact Strength | 101 – 113 kJ/m² | 48.1 – 53.8 ft-lb/in² | Average value: 108 kJ/m² Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.6 – 37.8 µm/m-°C | 17.0 – 21.0 µin/in-°F | Average value: 35.4 µm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | Average value: 182 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 – 183 °C | 345 – 362 °F | Average value: 178 °C Grade Count:13 |
| Flammability, UL94 | HB – V-0 | HB – V-0 | Average value: 3.50 Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1000 – 3.00e+16 ohm-cm | 1000 – 3.00e+16 ohm-cm | Average value: 7.45e+15 ohm-cm Grade Count:11 |
| Dielectric Constant | 3.15 – 3.50 | 3.15 – 3.50 | Average value: 3.37 Grade Count:6 |
| Dielectric Strength | 16.9 – 19.0 kV/mm | 430 – 483 kV/in | Average value: 17.8 kV/mm Grade Count:7 |
| Dissipation Factor | 0.000700 – 0.00800 | 0.000700 – 0.00800 | Average value: 0.00460 Grade Count:6 |
| Arc Resistance | 100 sec | 100 sec | Average value: 100 sec Grade Count:3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 332 – 399 °C | 630 – 750 °F | Average value: 356 °C Grade Count:13 |
| Mold Temperature | 93.3 – 163 °C | 200 – 325 °F | Average value: 126 °C Grade Count:13 |
| Drying Temperature | 135 – 191 °C | 275 – 376 °F | Average value: 141 °C Grade Count:13 |
| Moisture Content | 0.150 % | 0.150 % | Average value: 0.150 % Grade Count:10 |
| Dew Point | -31.7 °C | -25.0 °F | Average value: -31.7 °C Grade Count:10 |
| Injection Pressure | 68.9 – 124 MPa | 10000 – 18000 psi | Average value: 96.5 MPa Grade Count:10 |