Overview of materials for Polysulfone, 30% Glass Fiber Reinforced
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polysulfone, 30% Glass Fiber Reinforced”. Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 – 1.60 g/cc | 0.0527 – 0.0578 lb/in³ | Average value: 1.51 g/cc Grade Count:9 |
| Filler Content | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:4 |
| Water Absorption | 0.100 – 0.600 % | 0.100 – 0.600 % | Average value: 0.303 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00100 – 0.00300 cm/cm | 0.00100 – 0.00300 in/in | Average value: 0.00221 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00450 – 0.00600 cm/cm | 0.00450 – 0.00600 in/in | Average value: 0.00528 cm/cm Grade Count:3 |
| Melt Flow | 5.50 – 30.0 g/10 min | 5.50 – 30.0 g/10 min | Average value: 12.5 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 50.0 – 121 MPa | 7250 – 17500 psi | Average value: 104 MPa Grade Count:9 |
| 52.0 – 125 MPa
@Temperature 0.000 – 160 °C
|
7540 – 18100 psi
@Temperature 32.0 – 320 °F
|
Average value: 78.5 MPa Grade Count:2 | |
| 50.0 – 55.0 MPa
@Temperature 160 – 160 °C
|
7250 – 7980 psi
@Temperature 320 – 320 °F
|
Average value: 78.5 MPa Grade Count:1 | |
| 50.0 – 55.0 MPa
@Strain 1.00 – 1.70 %
|
7250 – 7980 psi
@Strain 1.00 – 1.70 %
|
Average value: 78.5 MPa Grade Count:1 | |
| Elongation at Break | 1.70 – 3.00 % | 1.70 – 3.00 % | Average value: 2.19 % Grade Count:9 |
| 1.60 – 1.80 %
@Temperature 60.0 – 150 °C
|
1.60 – 1.80 %
@Temperature 140 – 302 °F
|
Average value: 1.73 % Grade Count:1 | |
| Modulus of Elasticity | 8.00 – 9.00 GPa | 1160 – 1310 ksi | Average value: 8.56 GPa Grade Count:8 |
| 7.00 – 9.00 GPa
@Temperature 60.0 – 160 °C
|
1020 – 1310 ksi
@Temperature 140 – 320 °F
|
Average value: 7.94 GPa Grade Count:2 | |
| Flexural Yield Strength | 145 – 185 MPa | 21000 – 26800 psi | Average value: 162 MPa Grade Count:7 |
| Flexural Modulus | 7.58 – 9.38 GPa | 1100 – 1360 ksi | Average value: 8.04 GPa Grade Count:7 |
| Shear Modulus | 0.0250 – 0.950 GPa
@Temperature 50.0 – 200 °C
|
3.63 – 138 ksi
@Temperature 122 – 392 °F
|
Average value: 0.669 GPa Grade Count:1 |
| Izod Impact, Notched | 0.641 – 0.961 J/cm | 1.20 – 1.80 ft-lb/in | Average value: 0.770 J/cm Grade Count:7 |
| Izod Impact, Unnotched | 3.74 – 5.87 J/cm | 7.00 – 11.0 ft-lb/in | Average value: 4.60 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 7.00 – 7.00 kJ/m²
@Temperature -30.0 – -30.0 °C
|
3.33 – 3.33 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 7.00 kJ/m² Grade Count:1 |
| Izod Impact, Unnotched (ISO) | 36.0 – 50.0 kJ/m²
@Temperature -25.0 – 120 °C
|
17.1 – 23.8 ft-lb/in²
@Temperature -13.0 – 248 °F
|
Average value: 41.3 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 4.00 – 4.00 J/cm²
@Temperature -30.0 – -30.0 °C
|
19.0 – 19.0 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 4.00 J/cm² Grade Count:1 |
| Charpy Impact, Notched | 0.750 – 0.750 J/cm²
@Temperature -30.0 – -30.0 °C
|
3.57 – 3.57 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 0.750 J/cm² Grade Count:1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 – 25.0 µm/m-°C
@Temperature 140 – 180 °C
|
13.9 – 13.9 µin/in-°F
@Temperature 284 – 356 °F
|
Average value: 25.0 µm/m-°C Grade Count:1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 187 – 190 °C | 369 – 374 °F | Average value: 188 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 – 260 °C | 331 – 500 °F | Average value: 196 °C Grade Count:9 |
| Glass Transition Temp, Tg | 187 – 265 °C | 369 – 509 °F | Average value: 232 °C Grade Count:3 |
| Flammability, UL94 | V-1 – 5VA | V-1 – 5VA | Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 – 1.00e+16 ohm-cm | 1.00e+12 – 1.00e+16 ohm-cm | Average value: 3.34e+15 ohm-cm Grade Count:3 |
| Comparative Tracking Index | 125 – 250 V | 125 – 250 V | Average value: 161 V Grade Count:3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 – 410 °C | 520 – 770 °F | Average value: 352 °C Grade Count:9 |
| Mold Temperature | 93.3 – 210 °C | 200 – 410 °F | Average value: 153 °C Grade Count:8 |
| Drying Temperature | 110 – 170 °C | 230 – 338 °F | Average value: 145 °C Grade Count:8 |
| Moisture Content | 0.150 % | 0.150 % | Average value: 0.150 % Grade Count:4 |
| Dew Point | -31.7 °C | -25.0 °F | Average value: -31.7 °C Grade Count:4 |
| Injection Pressure | 68.9 – 138 MPa | 10000 – 20000 psi | Average value: 101 MPa Grade Count:5 |