Overview of materials for PVC, High Impact
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “PVC, High Impact”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.801 – 1.52 g/cc | 0.0289 – 0.0549 lb/in³ | Average value: 1.30 g/cc Grade Count:53 |
| Water Absorption | 0.200 – 3.00 % | 0.200 – 3.00 % | Average value: 2.07 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 – 0.00500 cm/cm | 0.00200 – 0.00500 in/in | Average value: 0.00350 cm/cm Grade Count:8 |
| Spiral Flow | 58.4 – 61.0 cm | 23.0 – 24.0 in | Average value: 59.1 cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 – 107 | 100 – 107 | Average value: 103 Grade Count:4 |
| Hardness, Shore D | 76.0 – 84.0 | 76.0 – 84.0 | Average value: 80.6 Grade Count:38 |
| Tensile Strength, Ultimate | 30.0 – 44.9 MPa | 4350 – 6510 psi | Average value: 41.3 MPa Grade Count:11 |
| Tensile Strength, Yield | 37.9 – 53.4 MPa | 5500 – 7750 psi | Average value: 45.0 MPa Grade Count:41 |
| Elongation at Break | 26.0 – 110 % | 26.0 – 110 % | Average value: 49.2 % Grade Count:10 |
| Elongation at Yield | 3.10 – 10.0 % | 3.10 – 10.0 % | Average value: 5.78 % Grade Count:4 |
| Modulus of Elasticity | 2.03 – 3.30 GPa | 294 – 479 ksi | Average value: 2.64 GPa Grade Count:50 |
| Flexural Yield Strength | 65.8 – 92.4 MPa | 9540 – 13400 psi | Average value: 78.9 MPa Grade Count:46 |
| Flexural Modulus | 2.05 – 3.21 GPa | 297 – 466 ksi | Average value: 2.66 GPa Grade Count:47 |
| Izod Impact, Notched | 0.600 – 13.9 J/cm | 1.12 – 26.0 ft-lb/in | Average value: 8.93 J/cm Grade Count:44 |
| 1.07 – 11.7 J/cm
@Temperature -40.0 – 10.0 °C
|
2.00 – 21.9 ft-lb/in
@Temperature -40.0 – 50.0 °F
|
Average value: 4.00 J/cm Grade Count:7 | |
| 1.07 – 11.7 J/cm
@Thickness 3.18 – 3.18 mm
|
2.00 – 21.9 ft-lb/in
@Thickness 0.125 – 0.125 in
|
Average value: 4.00 J/cm Grade Count:7 | |
| Dart Drop Total Energy | 44.5 – 280 J/cm | 0.0834 – 0.525 ft-lb/mil | Average value: 119 J/cm Grade Count:22 |
| 40.0 – 66.7 J/cm
@Temperature 0.000 – 0.000 °C
|
0.0749 – 0.125 ft-lb/mil
@Temperature 32.0 – 32.0 °F
|
Average value: 50.4 J/cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 – 140 µm/m-°C | 27.8 – 77.8 µin/in-°F | Average value: 71.1 µm/m-°C Grade Count:25 |
| Deflection Temperature at 0.46 MPa (66 psi) | 64.4 – 93.9 °C | 148 – 201 °F | Average value: 79.6 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 59.4 – 87.8 °C | 139 – 190 °F | Average value: 71.9 °C Grade Count:45 |
| Vicat Softening Point | 78.0 – 81.0 °C | 172 – 178 °F | Average value: 80.0 °C Grade Count:3 |
| Flammability, UL94 | V-0 – 5VA | V-0 – 5VA | Grade Count:11 |
| Oxygen Index | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:3 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 7.50 – 90.0 % | 7.50 – 90.0 % | Average value: 69.6 % Grade Count:6 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 196 – 213 °C | 385 – 415 °F | Average value: 205 °C Grade Count:5 |
| Melt Temperature | 174 – 210 °C | 345 – 410 °F | Average value: 196 °C Grade Count:29 |