Phillips 66 COPYLENE® CH043EW Polypropylene, Homopolymer, Slit Film, LWCO, Cordage
| Manufacturer | Phillips 66 |
| Trade Name | COPYLENE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
COPYLENE™ CH043EW is a medium flow polypropylene homopolymer resin suitable for general injection molding or extrusion applications. Applications: Raffia/tapes/strapping. Equivalent to Pro-fax® HL343KInformation provided by Phillips 66.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | ASTM D792 |
| Melt Flow | 4.3 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
4.3 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 36.5 MPa | 5300 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | ASTM D638 |
| Flexural Modulus | 1.59 GPa | 230 ksi | 0.05 in/min; 1% secant; Procedure A; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm
@Temperature 23.0 °C
|
0.700 ft-lb/in
@Temperature 73.4 °F
|
Method A; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Extrusion | |
| Injection Molding |