Plastcom PLASTALEN® PQ 81 T 20 Polypropylene reinforced with mineral filler, impact modified

Manufacturer Plastcom spol. s r.o.
Trade Name PLASTALEN®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union

Description

Material Notes:
Modified PP for injection molding with the content of 20% mineral filler. General application in all industry branches. Delivered in black color.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.05 g/cc

0.0379 lb/in³

STN EN ISO 1183-1
Filler Content 20 %

20 %

Linear Mold Shrinkage 0.0102 cm/cm

0.0102 in/in

STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0103 cm/cm

0.0103 in/in

STN EN ISO 294-4
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133

 

Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa

2180 psi

STN EN ISO 527-2
Elongation at Break 7.0 %

7.0 %

STN EN ISO 527-2
Tensile Modulus 1.50 GPa

218 ksi

STN EN ISO 527-2
Flexural Strength 17.0 MPa

2470 psi

STN EN ISO 178
Flexural Modulus 1.45 GPa

210 ksi

STN EN ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
STN EN ISO 179
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
STN EN ISO 179
Charpy Impact, Notched 2.00 J/cm²

@Temperature -20.0 °C
9.52 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
5.20 J/cm²

@Temperature 23.0 °C
24.7 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C

167 °F

STN EN ISO 75-2 (A)
Vicat Softening Point 125 °C

257 °F

STN EN ISO 306

 

Processing Properties Metric English Comments
Melt Temperature 200 – 250 °C

392 – 482 °F

Mold Temperature 40.0 – 50.0 °C

104 – 122 °F

Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Injection Pressure 70.0 – 120 MPa

10200 – 17400 psi

 

Descriptive Properties Value Comments
Color Black