Plastcom SLOVALEN PC 12 T 30 TS PP reinforced with 30% mineral filler
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Features: Modified copolymer PP for injection moulding or extrusion parts with the content of 30 % mineral filler. Increased rigidity, strength and impact strenght.Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stocking: The product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Linear Mold Shrinkage | 0.0125 cm/cm | 0.0125 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0117 cm/cm | 0.0117 in/in | |
| Melt Flow | 2.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
2.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| Elongation at Break | 20 % | 20 % | |
| Tensile Modulus | 2.75 GPa | 399 ksi | |
| Flexural Strength | 35.0 MPa | 5080 psi | |
| Flexural Modulus | 2.55 GPa | 370 ksi | |
| Charpy Impact Unnotched | 1.60 J/cm²
@Temperature -20.0 °C
|
7.61 ft-lb/in²
@Temperature -4.00 °F
|
|
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.300 J/cm²
@Temperature -20.0 °C
|
1.43 ft-lb/in²
@Temperature -4.00 °F
|
|
| 1.50 J/cm²
@Temperature 23.0 °C
|
7.14 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 153 °C | 307 °F | |
| Flammability Test | 1.0 | 1.0 | |
| Glow Wire Test | 550 °C | 1020 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 50.0 °C | 104 – 122 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |