Plastcom SLOVALEN PC 51 C 40 LS/1M Polypropylene reinforced with mineral filler, UV stabilized
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Modified copolymer PP for injection molding with the content of 40% mineral filler, UV stabilized. Product meets glow wire test at 750°C. Delivered in full RAL color scale.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage | 0.0136 cm/cm | 0.0136 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0156 cm/cm | 0.0156 in/in | STN EN ISO 294-4 |
| Melt Flow | 5.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
5.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | STN EN ISO 527-2 |
| Elongation at Break | 4.0 % | 4.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | STN EN ISO 527-2 |
| Flexural Strength | 25.0 MPa | 3630 psi | STN EN ISO 178 |
| Flexural Modulus | 1.60 GPa | 232 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm²
@Temperature -20.0 °C
|
9.52 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 5.00 J/cm²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature -20.0 °C
|
0.476 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 0.300 J/cm²
@Temperature 23.0 °C
|
1.43 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 °C | 302 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 150 °C | 302 °F | STN EN ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 750 °C
@Thickness 3.00 mm
|
1380 °F
@Thickness 0.118 in
|
STN EN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |