Plastcom SLOVALEN PH 51 T 15 Polypropylene Homopolymer, 15% Mineral Filled
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified homopolymer PP for injection moulding with the content of 15% mineral filler. Increased rigidity, strength and thermal use up to 130°C. Decreased shrinkage. General application in all industry branches – packing material, garden flower-pots, toys, furniture industry, dowels, clamps, hinge, office chairs, hangers, covers of car chassis, fenders, motors etc. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.023 g/cc | 0.03696 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0129 cm/cm | 0.0129 in/in | STN 64 0808 |
| Melt Flow | 5.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
5.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | STN EN ISO 527-2 |
| Elongation at Break | 5.0 % | 5.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | STN EN ISO 527-2 |
| Flexural Strength | 45.0 MPa | 6530 psi | STN EN ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 1.80 J/cm²
@Temperature -20.0 °C
|
8.57 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 5.50 J/cm²
@Temperature 23.0 °C
|
26.2 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm²
@Temperature -20.0 °C
|
0.952 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 0.300 J/cm²
@Temperature 23.0 °C
|
1.43 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | STN EN ISO 75/A |
| Vicat Softening Point | 160 °C | 320 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 50.0 °C | 104 – 122 °F | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |