Plastcom SLOVALEN PH 61 GF 30 Polypropylene Homopolymer, 30% Glass Fiber
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass fiber, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suitable for automotive, engineering, electrical and consumer goods industry. With the increasing content of GF also the toughness, tensile and bending strength, modulus in tension and bending increase and the shrinkage decreases as well as the heat application increases up to 130°C. Additional drying of the material is not necessary. Delivered in natural and in the full RAL color scale. Production of the fuel tank caps for the transport vehicles, shells for the textile industry.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0132 cm/cm | 0.0132 in/in | STN 64 0808 |
| Melt Flow | 10 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
10 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | STN EN ISO 527-2 |
| Elongation at Break | 4.0 % | 4.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 4.90 GPa | 711 ksi | STN EN ISO 527-2 |
| Flexural Strength | 85.0 MPa | 12300 psi | STN EN ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 1.00 J/cm²
@Temperature 23.0 °C
|
4.76 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 |
| 1.20 J/cm²
@Temperature -20.0 °C
|
5.71 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm²
@Temperature 23.0 °C
|
1.90 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | STN EN ISO 75/A |
| Vicat Softening Point | 130 °C | 266 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |