Plastcom SLOVALEN PH 69 GF 45 PP, 45% glass fibre
Manufacturer | Plastcom spol. s r.o. |
Trade Name | SLOVALEN |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 45% glass fibre, contains the modifier of mechanical properties.Thermo stable. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural mode and in the full RAL colour scale. Manufacturing of plastic nails for dowels, handles of radiator taps.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.10 g/cc | 0.0397 lb/in³ | |
Linear Mold Shrinkage | 0.0078 cm/cm | 0.0078 in/in | |
Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | |
Melt Flow | 8.0 g/10 min
@Load 0.325 kg,
Temperature 270 °C |
8.0 g/10 min
@Load 0.716 lb,
Temperature 518 °F |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 90.0 MPa | 13100 psi | |
Elongation at Break | 3.5 % | 3.5 % | |
Tensile Modulus | 7.70 GPa | 1120 ksi | |
Flexural Strength | 125 MPa | 18100 psi | |
Flexural Modulus | 6.20 GPa | 899 ksi | |
Charpy Impact Unnotched | 3.00 J/cm²
@Temperature -20.0 °C
|
14.3 ft-lb/in²
@Temperature -4.00 °F
|
|
3.50 J/cm²
@Temperature 23.0 °C
|
16.7 ft-lb/in²
@Temperature 73.4 °F
|
||
Charpy Impact, Notched | 0.500 J/cm²
@Temperature -20.0 °C
|
2.38 ft-lb/in²
@Temperature -4.00 °F
|
|
0.700 J/cm²
@Temperature 23.0 °C
|
3.33 ft-lb/in²
@Temperature 73.4 °F
|
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 160 °C | 320 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
Vicat Softening Point | 163 °C | 325 °F | B |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |