Plastics Group Polifil® GFRMPPCC-40 40% Glass Reinforced Polypropylene, High Impact
| Manufacturer | The Plastics Group of America |
| Trade Name | Polifil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Applications: AppliancesElectrical componentsAutomotiveUtility products Standard processing techniques are applicable. Information provided by The Plastics Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Filler Content | 40 % | 40 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.00030 cm/cm
@Thickness 1.59 mm
|
0.00030 in/in
@Thickness 0.0625 in
|
ASTM D955 |
| Melt Flow | 4.0 – 8.0 g/10 min | 4.0 – 8.0 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D638 |
| Flexural Modulus | 4.83 GPa | 700 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | At 73°F; ASTM D256 |
| Gardner Impact | 0.678 J | 0.500 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 305 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |