Plastics Group Polifil® T-30 30% Talc-Reinforced Polypropylene
| Manufacturer | The Plastics Group of America |
| Trade Name | Polifil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colorability, low shrinkage and yield maximum stiffness combined with characteristic impact.Applications: Automotive (underhood) applicationsMajor appliancesElectrical goodsHousewaresStandard processing techniques are applicable. Information provided by The Plastics Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.0090 cm/cm
@Thickness 1.59 mm
|
0.0090 in/in
@Thickness 0.0625 in
|
ASTM D955 |
| Melt Flow | 8.0 – 12 g/10 min | 8.0 – 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength at Break | 32.4 MPa | 4700 psi | ASTM D638 |
| Flexural Modulus | 2.41 GPa | 350 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | At 73°F; ASTM D256 |
| Izod Impact, Unnotched | 2.72 J/cm | 5.10 ft-lb/in | At 73°F; ASTM D256 |
| Gardner Impact | 0.565 J | 0.417 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |