Polykemi AB POLYfill PPH GF5035 PD2 VT Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled/Heat Resistant

Manufacturer Polykemi AB
Trade Name POLYfill
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union

Description

Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.17 g/cc

0.0423 lb/in³

ISO 1183
Filler Content 35 %

35 %

±2%; Polykemi
Linear Mold Shrinkage 0.0025 – 0.0035 cm/cm

0.0025 – 0.0035 in/in

Across Flow; ISO 2577
0.0025 – 0.0035 cm/cm

0.0025 – 0.0035 in/in

With Flow; ISO 2577
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133

 

Mechanical Properties Metric English Comments
Tensile Strength at Break <= 90.0 MPa

<= 13100 psi

ISO/R527
Elongation at Break 3.0 %

3.0 %

ISO/R527
Flexural Strength <= 130 MPa

<= 18900 psi

ISO 178
Flexural Modulus 6.00 GPa

@Temperature 23.0 °C
870 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 179
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179

 

Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C

320 °F

120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 145 °C

293 °F

120°C/h; ISO 75/1
Vicat Softening Point 130 °C

@Load 5.001 kg
266 °F

@Load 11.03 lb
50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
1380 °F

@Thickness 0.0787 in
IEC 695-2-1

 

Processing Properties Metric English Comments
Melt Temperature 205 – 260 °C

401 – 500 °F

Mold Temperature 40.0 – 80.0 °C

104 – 176 °F

Drying Temperature 70.0 – 80.0 °C

158 – 176 °F

Dry Time 2 – 4 hour

2 – 4 hour

in desiccant air dryer
2 – 4 hour

2 – 4 hour

in circulation dryer
Injection Pressure 40.0 – 110 MPa

5800 – 16000 psi

Back Pressure 1.00 – 2.00 MPa

145 – 290 psi

 

Descriptive Properties Value Comments
Holding Pressure () 20-40

% of injection pressure
Injection Speed () High