Polymer Resources PC/TP-GP2 PC Polyester, High Impact, Excellent Chemical Resistance (Unverified Data**)&
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 – 0.0090 cm/cm | 0.0060 – 0.0090 in/in | ASTM D955 |
| Melt Flow | 5.0 – 15 g/10 min | 5.0 – 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| 4.27 J/cm
@Temperature -40.0 °C
|
8.00 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 | |
| Gardner Impact | >= 36.2 J | >= 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/16 in |
| HB | HB | 1/8 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 – 271 °C | 480 – 520 °F | |
| Middle Barrel Temperature | 254 – 277 °C | 490 – 530 °F | |
| Front Barrel Temperature | 260 – 282 °C | 500 – 540 °F | |
| Melt Temperature | 246 – 274 °C | 475 – 525 °F | |
| Mold Temperature | 65.6 – 87.8 °C | 150 – 190 °F | |
| Drying Temperature | 104 – 110 °C | 220 – 230 °F | |
| Dry Time | 4 – 6 hour | 4 – 6 hour |