PolyOne Geon™ Vinyl Rigid Extrusion 87759 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Note: Finished part testing is required for ASTM E-84 certification. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 40.6 MPa | 5890 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.90 GPa | 421 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 69.6 MPa | 10100 psi | ASTM D790 |
| Flexural Modulus | 2.71 GPa | 393 ksi | ASTM D790 |
| Izod Impact, Notched | 1.90 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
3.56 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| 2.00 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
3.75 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| 2.30 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
4.31 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| Dart Drop Total Energy | 53.4 J/cm
@Temperature 23.0 °C
|
0.100 ft-lb/mil
@Temperature 73.4 °F
|
Procedure A, C.125; ASTM D4226 |
| 66.7 J/cm
@Temperature 23.0 °C
|
0.125 ft-lb/mil
@Temperature 73.4 °F
|
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C
@Thickness 3.18 mm
|
154 °F
@Thickness 0.125 in
|
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 – 193 °C | 360 – 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | ASTM E 84 | |
| Ease of Sizing | Good | |
| Features | Low Smoke Emission | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13253 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Profiles |