Polyram RamOfin PPH300G9 Polypropylene, 45% Glass Fiber
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
45% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0010 – 0.0030 cm/cm | 0.0010 – 0.0030 in/in | |
| Melt Flow | 4.5 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
4.5 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM-D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM-D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM-D790 |
| Flexural Strength | 140 MPa | 20300 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.10 J/cm
@Temperature 23.0 °C
|
2.06 ft-lb/in
@Temperature 73.4 °F
|
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | DIN 53461 |
| Flammability, UL94 | HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|