Premix Thermoplastics PRE-ELEC® ESD 6610 Static Dissipative Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® ESD 6610 is a static dissipative thermoplastic compound based on high impact polystyrene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 6610 has been developed for extrusion of thermoformable multilayer sheets and injection molding. It has been designed to full strict ionic purity requirements. Surface resistance values of 108 O (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. The products made out of PRE-ELEC® ESD 6610 are washable, reusable, recyclable. PRE-ELEC® ESD 6610 is whitish in colour and can be coloured into various bright colours.Applications: Injection moulded boxes, bins, thermoformed trays and clamshells when permanent ESD protection is required. These products can be used in electronics, medical, pharmaceutical and paper handling industries.Processing: PRE-ELEC® ESD 6610 compound can be processed in normal processing conditions as with polystyrene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.0060 – 0.0080 cm/cm | 0.0060 – 0.0080 in/in | ISO 294-4 |
| Melt Flow | 11 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
11 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70
@Thickness 1.00 mm
|
70
@Thickness 0.0394 in
|
ISO 868 |
| Tensile Strength | 16.0 MPa | 2320 psi | ISO 527 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
1.90 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
6.66 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | 75/Method Af |
| Vicat Softening Point | 84.0 °C | 183 °F | ISO 306/B50 |
| 98.0 °C | 208 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 ohm
@Thickness 0.00100 mm
|
1.00e+9 ohm
@Thickness 0.0000394 in
|
ISO IEC 61340-5-1 |
| Static Decay | <= 1.0 sec
@Thickness 1.00 mm
|
<= 1.0 sec
@Thickness 0.0394 in
|
ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 °C | 356 °F | Cylinder |
| 200 °C | 392 °F | Die | |
| Zone 2 | 190 °C | 374 °F | Cylinder |
| 200 °C | 392 °F | Die | |
| Zone 3 | 190 °C | 374 °F | Die |
| 200 °C | 392 °F | Cylinder | |
| Zone 4 | 200 °C | 392 °F | Die |
| 200 °C | 392 °F | Cylinder | |
| Zone 5 | 200 °C | 392 °F | Die |
| 200 °C | 392 °F | Cylinder | |
| Melt Temperature | 190 – 210 °C | 374 – 410 °F | |
| Mold Temperature | 30.0 – 70.0 °C | 86.0 – 158 °F | |
| Roll Temperature | 50.0 °C | 122 °F | 3rd Roll |
| 60.0 °C | 140 °F | 1st Roll | |
| 60.0 °C | 140 °F | 2nd Roll | |
| Drying Temperature | 70.0 – 80.0 °C | 158 – 176 °F | Pre-drying in a dehumidifier |
| Dry Time | 3 – 4 hour | 3 – 4 hour | |
| Injection Pressure | 75.2 – 120 MPa | 10900 – 17400 psi | |
| Hold Pressure | 40.0 – 60.0 MPa | 5800 – 8700 psi | Post Pressure |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate |