Raschig Group 3535 Epoxy
| Manufacturer | Raschig Group |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate packed in moisture resistant cartons, Standard carton size: 25 kg palletized in 750 kg loads. Processing: Compression/Transfer/Injection. Applications: Connectors, Thermocouples, Sensors, Resistors, Potentiometers.Information provided by the Raschig Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.90 – 2.10 g/cc | 1.90 – 2.10 g/cc | ISO 1183 |
| Apparent Bulk Density | 0.850 – 1.00 g/cc | 0.0307 – 0.0361 lb/in³ | ISO 60 |
| Water Absorption | <= 0.10 %
@Temperature 23.0 °C,
Time 86400 sec |
<= 0.10 %
@Temperature 73.4 °F,
Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0030 – 0.0050 cm/cm | 0.0030 – 0.0050 in/in | (longitudinal) Injection and Compression; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 – 70.0 MPa | 8700 – 10200 psi | Injection and Compression; ISO 527 |
| Modulus of Elasticity | 15.0 – 18.0 GPa | 2180 – 2610 ksi | Injection and Compression; ISO 527 |
| Flexural Strength | 120 – 140 MPa | 17400 – 20300 psi | Injection and Compression; ISO 178 |
| Flexural Modulus | 14.0 – 16.0 GPa | 2030 – 2320 ksi | Injection and Compression; ISO 178 |
| Compressive Strength | 150 – 200 MPa | 21800 – 29000 psi | ISO 604 |
| Charpy Impact Unnotched | 0.800 – 1.20 J/cm²
@Temperature 23.0 °C
|
3.81 – 5.71 ft-lb/in²
@Temperature 73.4 °F
|
Injection and Compression; ISO 179/ 1eU |
| Charpy Impact, Notched | 0.250 – 0.350 J/cm²
@Temperature 23.0 °C
|
1.19 – 1.67 ft-lb/in²
@Temperature 73.4 °F
|
Injection and Compression; ISO 179/ 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 – 20.0 µm/m-°C
@Temperature 50.0 – 150 °C
|
8.33 – 11.1 µin/in-°F
@Temperature 122 – 302 °F
|
ISO 11359-2 |
| Thermal Conductivity | 0.600 – 0.800 W/m-K | 4.16 – 5.55 BTU-in/hr-ft²-°F | ASTM E1461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | Injection; ISO 75-A |
| Deflection Temperature at 8.0 MPa | 170 – 190 °C | 338 – 374 °F | Injection; ISO 75-C |
| Flammability, UL94 | V-0
@Thickness 5.70 mm
|
V-0
@Thickness 0.224 in
|
|
| Shrinkage | <= 0.050 %
@Temperature 110 °C,
Time 605000 sec |
<= 0.050 %
@Temperature 230 °F,
Time 168 hour |
Post-shrinkage; ISO 2577 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 – 1.00e+16 ohm-cm | 1.00e+15 – 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 – 1.00e+15 ohm | 1.00e+14 – 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.0 – 6.0
@Frequency 1.00e+6 Hz
|
4.0 – 6.0
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 5.0 – 7.0
@Frequency 100 Hz
|
5.0 – 7.0
@Frequency 100 Hz
|
IEC 60250 | |
| Dielectric Strength | 0.984 – 1.38 kV/mm | 25.0 – 35.0 kV/in | IEC 60243-1 |
| 15.0 – 20.0 kV/mm
@Thickness 1.00 mm
|
381 – 508 kV/in
@Thickness 0.0394 in
|
IEC 60243-1 | |
| Dissipation Factor | 0.010 – 0.030
@Frequency 100 Hz
|
0.010 – 0.030
@Frequency 100 Hz
|
IEC 60250 |
| 0.010 – 0.030
@Frequency 1.00e+6 Hz
|
0.010 – 0.030
@Frequency 1.00e+6 Hz
|
IEC 60250 | |
| Comparative Tracking Index | >= 250 V | >= 250 V | CTI; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 6.00 Month
@Temperature 15.0 – 25.0 °C
|
6.00 Month
@Temperature 59.0 – 77.0 °F
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| Arc Resistance | 4 Stufe | ASTM D495 |
| Glow wire flammability test | 900/1 | IEC 60695 2-12 |
| Glow wire ignitability test | 900/1 | IEC 60695 2-13 |
| Water Absorption | <10 mg | ISO 62; 24h / 23°C |