Raschig Group EPOXIDUR® 3582 EP Epoxy
| Manufacturer | Raschig Group |
| Trade Name | EPOXIDUR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Molding compound with a broad spectrum of applications. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression moldingInformation provided by the Raschig Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.90 – 2.00 g/cc | 1.90 – 2.00 g/cc | ISO 1183 |
| Apparent Bulk Density | 0.700 – 1.00 g/cc | 0.0253 – 0.0361 lb/in³ | ISO 60 |
| Water Absorption | <= 0.100 %
@Temperature 23.0 °C,
Time 86400 sec |
<= 0.100 %
@Temperature 73.4 °F,
Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0030 – 0.0050 cm/cm | 0.0030 – 0.0050 in/in | (longitudinal) Injection and Compression; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 – 80.0 MPa | 8700 – 11600 psi | Injection and Compression; ISO 527 |
| Modulus of Elasticity | 15.0 – 18.0 GPa | 2180 – 2610 ksi | Injection and Compression; ISO 527 |
| Flexural Strength | 180 – 210 MPa | 26100 – 30500 psi | Injection and Compression; ISO 178 |
| Flexural Modulus | 20.0 – 23.0 GPa | 2900 – 3340 ksi | Injection and Compression; ISO 178 |
| Compressive Strength | 200 – 250 MPa | 29000 – 36300 psi | ISO 604 |
| Charpy Impact Unnotched | 1.20 – 1.60 J/cm²
@Temperature 23.0 °C
|
5.71 – 7.61 ft-lb/in²
@Temperature 73.4 °F
|
Injection and Compression; ISO 179/ 1eU |
| Charpy Impact, Notched | 0.400 – 0.700 J/cm²
@Temperature 23.0 °C
|
1.90 – 3.33 ft-lb/in²
@Temperature 73.4 °F
|
Injection and Compression; ISO 179/ 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 – 20.0 µm/m-°C
@Temperature 50.0 – 150 °C
|
8.33 – 11.1 µin/in-°F
@Temperature 122 – 302 °F
|
ISO 11359-2 |
| Thermal Conductivity | 0.400 – 0.600 W/m-K | 2.78 – 4.16 BTU-in/hr-ft²-°F | ASTM E1461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | Injection and Compression; ISO 75-A |
| Deflection Temperature at 8.0 MPa | 180 – 200 °C | 356 – 392 °F | Injection and Compression; ISO 75-C |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| Shrinkage | <= 0.0500 %
@Temperature 110 °C,
Time 605000 sec |
<= 0.0500 %
@Temperature 230 °F,
Time 168 hour |
ISO 2577 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 – 1.00e+16 ohm-cm | 1.00e+15 – 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 – 1.00e+15 ohm | 1.00e+14 – 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.0 – 6.0
@Frequency 100 Hz
|
4.0 – 6.0
@Frequency 100 Hz
|
IEC 60250 |
| 4.0 – 6.0
@Frequency 1.00e+6 Hz
|
4.0 – 6.0
@Frequency 1.00e+6 Hz
|
IEC 60250 | |
| Dielectric Strength | 20.0 – 30.0 kV/mm | 508 – 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 – 0.020
@Frequency 100 Hz
|
0.010 – 0.020
@Frequency 100 Hz
|
IEC 60250 |
| 0.020 – 0.040
@Frequency 1.00e+6 Hz
|
0.020 – 0.040
@Frequency 1.00e+6 Hz
|
IEC 60250 | |
| Comparative Tracking Index | >= 250 V | >= 250 V | CTI; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 6.00 Month
@Temperature <=20.0 °C
|
6.00 Month
@Temperature <=68.0 °F
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| Arc Resistance | 4 Stufe | ASTM D495 |
| Glow wire flammability test | 900/1 | IEC 60695 2-12 |
| Glow wire ignitability test | 900/1 | IEC 60695 2-13 |
| Water Absorption | <10 mg | 24h/23°C; ISO 62 |