SABIC Innovative Plastics LNP LUBRICOMP ZFL31XXC PPE+PS
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LNP* LUBRICOMP* ZFL31XXC is a compound based on PPE+PS resin containing 5% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 – 0.0070 cm/cm
@Time 86400 sec
|
0.0050 – 0.0070 in/in
@Time 24.0 hour
|
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 – 0.0080 cm/cm
@Time 86400 sec
|
0.0060 – 0.0080 in/in
@Time 24.0 hour
|
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.64 GPa | 528 ksi | 1 mm/min; ISO 527 |
| 4.01 GPa | 582 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 89.0 MPa | 12900 psi | ISO 178 |
| 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.65 GPa | 529 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.80 J/cm | 7.12 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J
@Temperature 23.0 °C
|
8.85 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.26 | 0.26 | ASTM D3702 Modified |
| K (wear) Factor | 201 x 10-8 mm³/N-M | 100 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.7 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
36.5 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
ASTM D696 |
| CTE, linear, Transverse to Flow | 68.5 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
38.1 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 136 °C
@Thickness 3.20 mm
|
277 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 127 °C
@Thickness 3.20 mm
|
261 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |