SABIC Innovative Plastics LNP STAT-LOY 63000CTC PC+POLYESTER (Asia Pacific)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 140 % | 140 % | 5 mm/min; ISO 527 |
| 200 % | 200 % | Type I, 10 mm/min; SABIC – Japan Method | |
| Tensile Modulus | 1.17 GPa | 170 ksi | 50 mm/min; ASTM D638 |
| 1.19 GPa | 173 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 52.0 MPa | 7540 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.15 GPa | 167 ksi | 2 mm/min; ISO 178 |
| 1.17 GPa | 170 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.80 J/cm | 10.9 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 6.90 J/cm² | 32.8 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
66.7 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
77.8 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C
@Thickness 6.40 mm
|
183 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C
@Thickness 6.40 mm
|
167 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 25 %
@Thickness 2.54 mm
|
25 %
@Thickness 0.100 in
|
ASTM D1003 |
| Transmission, Visible | 77 % | 77 % | 2.54 mm; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+9 – 3.00e+11 ohm-cm | 8.00e+9 – 3.00e+11 ohm-cm | ASTM D257 |
| Surface Resistance | 9.00e+9 – 4.00e+11 ohm | 9.00e+9 – 4.00e+11 ohm | ASTM D257 |
| Static Decay | 2.0 sec | 2.0 sec | 5000V to <50V; FTMS101B |