SABIC Innovative Plastics NORYL 725A PPE+HIPS (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
NORYL 725A is an unfilled material, with a Vicat B/120 of 135°C according ISO 306. NORYL 725A has been designed for use in automotive interior applications, where anti-squeak is required.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.22 % | 0.22 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 – 0.0070 cm/cm | 0.0050 – 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 10 g/10 min
@Load 5.00 kg,
Temperature 280 °C |
10 g/10 min
@Load 11.0 lb,
Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 45 % | 45 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m²
@Temperature -30.0 °C
|
4.28 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm²
@Temperature -30.0 °C
|
4.76 ft-lb/in²
@Temperature -22.0 °F
|
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 40 | 40 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
38.9 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
50.0 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-2 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ISO 306 |
| 135 °C | 275 °F | Rate B/120; ISO 306 | |
| 140 °C | 284 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
UL 94 by SABIC-IP |
| Oxygen Index | 22 % | 22 % | ISO 4589 |
| Glow Wire Test | 650 °C
@Thickness 3.20 mm
|
1200 °F
@Thickness 0.126 in
|
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.5
@Frequency 1.00e+6 Hz
|
2.5
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 2.5
@Frequency 50.0 – 60.0 Hz
|
2.5
@Frequency 50.0 – 60.0 Hz
|
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm
@Thickness 3.20 mm
|
432 kV/in
@Thickness 0.126 in
|
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0010
@Frequency 1.00e+6 Hz
|
0.0010
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 0.0030
@Frequency 50.0 – 60.0 Hz
|
0.0030
@Frequency 50.0 – 60.0 Hz
|
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |