SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Noryl* CRX2201 resin is a 25% mineral reinforced, injection moldable modified polyphenylene ether resin designed for improved chemical resistance when compared with standard Noryl resins. Noryl CRX2201 resin uses non chlorinated, non brominated FR additives to deliver a UL94 V1 rating at 1.5 mm. Noryl CRX2201 may be an excellent material candidate where flame resistance and dimensional stability are required.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D 792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.020 %
@Temperature 23.0 °C
|
0.020 %
@Temperature 73.4 °F
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 – 0.0050 cm/cm
@Thickness 3.20 mm
|
0.0030 – 0.0050 in/in
@Thickness 0.126 in
|
SABIC Method |
| Melt Flow | 6.0 g/10 min
@Load 5.00 kg,
Temperature 280 °C |
6.0 g/10 min
@Load 11.0 lb,
Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 8.0 g/10 min
@Load 5.00 kg,
Temperature 280 °C |
8.0 g/10 min
@Load 11.0 lb,
Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
| 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
| 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 5.50 GPa | 798 ksi | 1 mm/min; ISO 527 |
| 5.60 GPa | 812 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 119 MPa | 17300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 120 MPa | 17400 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 6.10 GPa | 885 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.260 J/cm
@Temperature -30.0 °C
|
0.487 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 0.320 J/cm
@Temperature 23.0 °C
|
0.599 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m²
@Temperature -30.0 °C
|
0.952 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A |
| 2.00 kJ/m²
@Temperature 23.0 °C
|
0.952 ft-lb/in²
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature 23.0 °C
|
0.476 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 3.00 J
@Temperature 23.0 °C
|
2.21 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
17.8 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 |
| 34.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
18.9 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
30.0 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 60.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
33.3 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C
@Thickness 3.20 mm
|
226 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Vicat Softening Point | 124 °C | 255 °F | Rate B/50; ASTM D 1525 |
| 124 °C | 255 °F | Rate B/50; ISO 306 | |
| 127 °C | 261 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-1
@Thickness 1.50 mm
|
V-1
@Thickness 0.0591 in
|
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 5.00e+16 ohm | 5.00e+16 ohm | ASTM D 257 |
| Dielectric Constant | 2.9
@Frequency 50.0 – 60.0 Hz
|
2.9
@Frequency 50.0 – 60.0 Hz
|
ASTM D 150 |
| Dielectric Strength | 27.0 kV/mm
@Thickness 3.20 mm
|
686 kV/in
@Thickness 0.126 in
|
in oil; ASTM D 149 |
| Dissipation Factor | 0.0070
@Frequency 50.0 – 60.0 Hz
|
0.0070
@Frequency 50.0 – 60.0 Hz
|
ASTM D 150 |