SABIC Innovative Plastics NORYL NH5110E PPE+PS (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
NORYL NH5110E is a flame retardant, non halogenated, impact modified extrusion grade. Developed for low beard-growth, with a Vicat B/120 of 138 Deg C, according to ISO 306 and a UL-94 rating of V1@ 1.5mm, it would be suitable for electrical conduit and cable management applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Melt Index of Compound | 9.0 g/10 min
@Load 5.00 kg,
Temperature 280 °C |
9.0 g/10 min
@Load 11.0 lb,
Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 18 % | 18 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m²
@Temperature -30.0 °C
|
4.28 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.10 J/cm²
@Temperature -30.0 °C
|
5.23 ft-lb/in²
@Temperature -22.0 °F
|
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 82.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
45.6 µin/in-°F
@Temperature 73.4 – 176 °F
|
ASTM E 831 |
| 82.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
45.6 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
52.2 µin/in-°F
@Temperature 73.4 – 176 °F
|
ASTM E 831 |
| 94.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
52.2 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/120; ISO 306 |
| 149 °C | 300 °F | Rate B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-1
@Thickness 1.50 mm
|
V-1
@Thickness 0.0591 in
|
UL 94 |
| Oxygen Index | 34 % | 34 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.6
@Frequency 1.00e+6 Hz
|
2.6
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 2.6
@Frequency 1.00e+6 Hz
|
2.6
@Frequency 1.00e+6 Hz
|
IEC 60250 | |
| Dielectric Strength | 46.0 kV/mm
@Thickness 1.00 mm
|
1170 kV/in
@Thickness 0.0394 in
|
short time; IEC 60243-1 |
| Dissipation Factor | 0.0017
@Frequency 1.00e+6 Hz
|
0.0017
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 0.0017
@Frequency 1.00e+6 Hz
|
0.0017
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Pass | IEC 60695-10-2 |