SABIC Innovative Plastics Noryl PC180X PPE+PS
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Nonbrominated, nonchlorinated flame retardant. V-1/5VA rated; 175F (90C) HDT. Improved productivity and reliability.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 – 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 – 0.0070 cm/cm | 0.0050 – 0.0070 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D 785 |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 22 % | 22 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.900 J/cm
@Temperature -30.0 °C
|
1.69 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 3.09 J/cm
@Temperature 23.0 °C
|
5.79 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Unnotched | 11.74 J/cm
@Temperature 23.0 °C
|
21.99 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 |
| Impact Test | 3.00 J
@Temperature 23.0 °C
|
2.21 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 64
@Load 1.00 kg
|
64
@Load 2.20 lb
|
CS-17; ASTM D 1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C
@Thickness 6.40 mm
|
194 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C
@Thickness 6.40 mm
|
174 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-2
@Thickness 1.47 mm
|
V-2
@Thickness 0.0579 in
|
UL 94 |
| V-1
@Thickness 2.99 mm
|
V-1
@Thickness 0.118 in
|
UL 94 | |
| 5VA
@Thickness 3.81 mm
|
5VA
@Thickness 0.150 in
|
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.30e+16 ohm-cm | 3.30e+16 ohm-cm | ASTM D 257 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D 257 |
| Dielectric Constant | 2.53
@Frequency 1.00e+6 Hz
|
2.53
@Frequency 1.00e+6 Hz
|
ASTM D 150 |
| 2.67
@Frequency 50.0 – 60.0 Hz
|
2.67
@Frequency 50.0 – 60.0 Hz
|
ASTM D 150 | |
| Dielectric Strength | 17.7 kV/mm
@Thickness 3.20 mm
|
450 kV/in
@Thickness 0.126 in
|
in oil; ASTM D 149 |
| Dissipation Factor | 0.0026
@Frequency 1.00e+6 Hz
|
0.0026
@Frequency 1.00e+6 Hz
|
ASTM D 150 |
| 0.012
@Frequency 50.0 – 60.0 Hz
|
0.012
@Frequency 50.0 – 60.0 Hz
|
ASTM D 150 | |
| Arc Resistance | 60 – 120 sec | 60 – 120 sec | Tungsten, PLC code 6; ASTM D 495 |
| Comparative Tracking Index | 250 – 400 V | 250 – 400 V | PLC code 2; UL 746A |
| Hot Wire Ignition, HWI | 30 – 60 sec | 30 – 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | 15 – 30 arcs | 15 – 30 arcs | surface, PLC code 3; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |