SABIC Innovative Plastics Noryl PX4058 PPE+PS
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PPO, polyolefin blend. Improved chemical resistance. 253F (125C) HDT.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Water Absorption | 0.070 %
@Time 86400 sec
|
0.070 %
@Time 24.0 hour
|
ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D 785 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 114 % | 114 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.49 J/cm
@Temperature -40.0 °C
|
2.79 ft-lb/in
@Temperature -40.0 °F
|
ASTM D 256 |
| 4.80 J/cm
@Temperature 23.0 °C
|
8.99 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Unnotched | 2.67 J/cm
@Temperature -30.0 °C
|
5.00 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 4812 |
| 19.81 J/cm
@Temperature 23.0 °C
|
37.11 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 | |
| Impact Test | 2.00 J
@Temperature 23.0 °C
|
1.48 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Energy @ peak; ASTM D 3763 |
| 2.00 J
@Temperature -30.0 °C
|
1.48 ft-lb
@Temperature -22.0 °F
|
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Taber Abrasion, mg/1000 Cycles | 8.0
@Load 1.00 kg
|
8.0
@Load 2.20 lb
|
CS-17; ASTM D 1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C
@Thickness 6.40 mm
|
284 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C
@Thickness 6.40 mm
|
252 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 |