SABIC Innovative Plastics NORYL V01550 PPE+HIPS (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
NORYL V01550 is a 15 % short glass fibre reinforced, flame retardant material with a HDT/A of 130C according ISO 75. NORYL V01550 is V0 at 0.75 mm according UL94 and is halogen free according VDE/DIN 472 part 815. NORYL V01550 is designed for electronic and electrical applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 – 0.0050 cm/cm | 0.0030 – 0.0050 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 7.0 g/10 min
@Load 5.00 kg,
Temperature 280 °C |
7.0 g/10 min
@Load 11.0 lb,
Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 10 g/10 min
@Load 5.00 kg,
Temperature 300 °C |
10 g/10 min
@Load 11.0 lb,
Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 130 MPa | 18900 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| 45.0 kJ/m²
@Temperature -30.0 °C
|
21.4 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 4.50 J/cm²
@Temperature -30.0 °C
|
21.4 ft-lb/in²
@Temperature -22.0 °F
|
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Taber Abrasion, mg/1000 Cycles | 50 | 50 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
22.2 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
33.3 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-2 |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 145 °C | <= 293 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 150 °C | 302 °F | Rate B/50; ISO 306 |
| 155 °C | 311 °F | Rate B/120; ISO 306 | |
| 160 °C | 320 °F | Rate A/50; ISO 306 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-0
@Thickness 0.750 mm
|
V-0
@Thickness 0.0295 in
|
UL 94 |
| 5VA
@Thickness 3.00 mm
|
5VA
@Thickness 0.118 in
|
UL 94 | |
| Oxygen Index | 32 % | 32 % | ISO 4589 |
| Glow Wire Test | 960 °C
@Thickness 3.20 mm
|
1760 °F
@Thickness 0.126 in
|
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.0
@Frequency 1.00e+6 Hz
|
3.0
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 3.1
@Frequency 50.0 – 60.0 Hz
|
3.1
@Frequency 50.0 – 60.0 Hz
|
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm
@Thickness 3.20 mm
|
406 kV/in
@Thickness 0.126 in
|
in oil; IEC 60243-1 |
| 26.0 kV/mm
@Thickness 1.60 mm
|
660 kV/in
@Thickness 0.0630 in
|
in oil; IEC 60243-1 | |
| 33.0 kV/mm
@Thickness 0.800 mm
|
838 kV/in
@Thickness 0.0315 in
|
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0030
@Frequency 1.00e+6 Hz
|
0.0030
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 0.0050
@Frequency 50.0 – 60.0 Hz
|
0.0050
@Frequency 50.0 – 60.0 Hz
|
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |