Samsung Cheil Industries Starex® WR-9310 ASA, Unreinforced Heat Resistant
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Heat resistant ASA that is used in the interior/exterior material of automobileInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0070 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 10 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
10 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 45.1 MPa | 6540 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 58.8 MPa | 8530 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 3.43 J/cm
@Thickness 3.17 mm
|
6.43 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C
@Thickness 6.40 mm
|
190 °F
@Thickness 0.252 in
|
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |