Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK) (Unverified Data**)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire AV-848 CF30 is a 30% carbon fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of PEEK. These include: improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 CF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire AV-848 CF30 can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion.Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Carbon Fiber Reinforcement |
| Water Absorption | 0.10 %
@Time 86400 sec
|
0.10 %
@Time 24.0 hour
|
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00 – 0.0020 cm/cm | 0.00 – 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 – 0.0060 cm/cm | 0.0040 – 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min
@Load 2.16 kg,
Temperature 400 °C |
3.5 g/10 min
@Load 4.76 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 176 MPa | 25500 psi | 5.0 mm/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | 5.0 mm/min; ASTM D638 |
| Tensile Modulus | 18.8 GPa | 2730 ksi | 5.0 mm/min; ASTM D638 |
| Flexural Strength | 259 MPa | 37600 psi | ASTM D790 |
| Flexural Modulus | 16.5 GPa | 2390 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Shear Strength | 95.0 MPa | 13800 psi | ASTM D732 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.0370 W/m-K | 0.257 BTU-in/hr-ft²-°F | ASTM E1530 |
| Melting Point | 340 °C | 644 °F | Peak; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 382 – 404 °C | 720 – 759 °F | |
| Mold Temperature | 166 – 193 °C | 331 – 379 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Fatigue Resistant | |
| Flame Retardant | ||
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| High Heat Resistance | ||
| High Stiffness | ||
| High Strength | ||
| Forms | Pellets | |
| Generic | PAEK | |
| Injection Rate | Fast | |
| Processing Method | Injection Molding | |
| Machining | ||
| Profile Extrusion | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 | |
| Uses | Bearings | |
| Bushings | ||
| Oil/Gas Applications | ||
| Seals | ||
| Wear Strip |