Solvay Specialty Polymers Supradel® HTS-2430 High Temperature Sulfone Resin (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
SUPRADEL HTS-2420 is a 20% glass-fiber reinforced high-temperature, high-performance, amorphous, sulfone polymer. With a glass transition temperature of 245°C and a heat deflection temperature of 240°C, SUPRADEL HTS-2420 resin this resin extends the thermal capability range available to design engineers in other sulfone polymers. The resin is completely amorphous and fully thermoplastic allowing easy melt fabrication by means of operations such as injection molding and extrusion. Along with its high thermal performance capabilities, SUPRADEL HTS-2420 resin also has a long list of high-performance attributes which include excellent hydrolytic stability, resistance to acids and bases, and inherent flame retardance. SUPRADEL HTS-2420 resin is easily amenable to fabrication by injection molding, and other thermoplastic fabrication techniques. By virtue of its very high temperature performance and the unique combination of other engineering attributes, SUPRADEL HTS-2420 resin constitutes a good candidate for metal replacement as well as non-thermoplastic resin replacement in a wide range of engineering applications. SUPRADEL HTS-2420 resin is available in natural and black.Information provided by Solvay Advanced Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | At 24 hours; ASTM D570 |
| Water Absorption at Saturation | 1.2 % | 1.2 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 7.5 g/10 min
@Load 5.00 kg,
Temperature 400 °C |
7.5 g/10 min
@Load 11.0 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 16900 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | ASTM D638 |
| Flexural Strength | 174 MPa | 25200 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Annealed 0.125 inch thick specimen; ASTM D648 |
| Glass Transition Temp, Tg | 245 °C | 473 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 390 – 410 °C | 734 – 770 °F | Stock Temperature |
| Mold Temperature | >= 180 °C | >= 356 °F | |
| 190 – 210 °C | 374 – 410 °F | Long flow or thin wall parts or for low residual stress | |
| Drying Temperature | 150 °C | 302 °F | 2.5 hours for injection molding |
| 170 °C | 338 °F | > 4 hours hopper drying with desiccated air inlet for extrusion |