Solvay Specialty Polymers Supradel® HTS-2630 High Temperature Sulfone Resin (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
SUPRADEL HTS-2630 is a 30% glass-fiber reinforced high-temperature, high-performance, amorphous, sulfone polymer.In addition to exceptional thermal performance, this resin has the other performance features and attributes traditionally known for sulfone polymers. These features include good strength, stiffness, and dielectric properties over a wide temperature range, resistance to hydrolysis by hot water and steam environments, excellent resistance to acids and bases, and inherent flammability resistance. The resin also offers a high degree of dimensional control during fabrication and dimensional stability during part service life.SUPRADEL HTS-2630 resin is easily amenable to fabrication by injection molding, and other thermoplastic fabrication techniques. By virtue of its very high temperature performance and the unique combination of other engineering attributes, SUPRADEL HTS-2630 resin constitutes a good candidate for metal replacement as well as non-thermoplastic resin replacement in a wide range of engineering applications. SUPRADEL HTS-2630 resin is available in natural and black.Information provided by Solvay Advanced Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | At 24 hours; ASTM D570 |
| Water Absorption at Saturation | 1.5 % | 1.5 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 5.5 g/10 min
@Load 5.00 kg,
Temperature 400 °C |
5.5 g/10 min
@Load 11.0 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 112 MPa | 16300 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | ASTM D638 |
| Flexural Strength | 164 MPa | 23800 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Annealed 0.125 inch thick specimen; ASTM D648 |
| Glass Transition Temp, Tg | 265 °C | 509 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 390 – 410 °C | 734 – 770 °F | Stock Temperature |
| Mold Temperature | >= 180 °C | >= 356 °F | |
| 190 – 210 °C | 374 – 410 °F | Long flow or thin wall parts or for low residual stress | |
| Drying Temperature | 150 °C | 302 °F | 2.5 hours for injection molding |
| 170 °C | 338 °F | > 4 hours hopper drying with desiccated air inlet for extrusion |