Solvay Specialty Polymers Udel® GF-130 Polysulfone (PSU), Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Udel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Udel® GF-130, resin is a 30% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties and attractive price make these resins particularly effective alternatives to metals in many engineering applications.Features: Acid Resistant; Alcohol Resistant; Alkali Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Strength; High Heat Resistance; High Rigidity; Hydrocarbon Resistant; Hydrolytically StableUses: Appliance Components; Appliances; Automotive Electronics; Electrical Parts; Electrical/Electronic Applications; Food Service Applications; Industrial Parts; Microwave Cookware; Piping; Plumbing Parts; Valves/Valve PartsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | |
| Melt Flow | 6.5 g/10 min
@Load 2.16 kg,
Temperature 343 °C |
6.5 g/10 min
@Load 4.76 lb,
Temperature 649 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 108 MPa | 15700 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 8.69 GPa | 1260 ksi | ASTM D638 |
| Flexural Strength | 154 MPa | 22300 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 113 kJ/m² | 53.8 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 181 °C | 358 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0
@Thickness 3.18 mm
|
V-0
@Thickness 0.125 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.47
@Frequency 1.00e+6 Hz
|
3.47
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.48
@Frequency 60.0 Hz
|
3.48
@Frequency 60.0 Hz
|
ASTM D150 | |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.00070
@Frequency 60.0 Hz
|
0.00070
@Frequency 60.0 Hz
|
ASTM D150 |
| 0.0050
@Frequency 1.00e+6 Hz
|
0.0050
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| NSF | Yes | Yes | NSF 61 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 – 399 °C | 649 – 750 °F | |
| Mold Temperature | 121 – 163 °C | 250 – 325 °F | |
| Drying Temperature | 163 – 191 °C
@Time 10800 – 14400 sec
|
325 – 376 °F
@Time 3.00 – 4.00 hour
|
|
| Back Pressure | 0.345 – 0.689 MPa | 50.0 – 99.9 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | ISO 10993; ISO 10993-Part 1 | |
| Availability | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural; Opaque | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Extrusion; Injection Molding | |
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.0:1.0 |