Spartech EP6240 Filled and Reinforced Copolymer
| Manufacturer | Spartech |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Filled copolymers offer a higher level of impact performance than homopolymer materials, and higher stiffness than unfilled copolymers. Copolymer based materials retain much of their impact strength at low temperatures. Typical applications include thermoformed frozen food containers, extruded and blow molded automotive and construction materials, and blow molded recreational equipment.Information provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc
@Temperature 22.8 °C
|
1.25 g/cc
@Temperature 73.0 °F
|
ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | 0.125inch wall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 1.38 GPa | 200 ksi | secant; ASTM D790 |
| 1.93 GPa | 280 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 1.60 J/cm
@Temperature 22.8 °C
|
3.00 ft-lb/in
@Temperature 73.0 °F
|
ASTM D256 |
| Gardner Impact | 8.13 J
@Temperature -5.56 °C
|
6.00 ft-lb
@Temperature 22.0 °F
|
ASTM D5420 |
| >= 33.9 J
@Temperature 22.8 °C
|
>= 25.0 ft-lb
@Temperature 73.0 °F
|
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 55 % | 55 % | 60°; ASTM D523 |