Spartech PP5120 Talc Filled Homopolymer
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc
@Temperature 22.8 °C
|
1.04 g/cc
@Temperature 73.0 °F
|
ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | 0.125inch wall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 1.90 GPa | 275 ksi | secant; ASTM D790 |
| 2.48 GPa | 360 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm
@Temperature 22.8 °C
|
0.600 ft-lb/in
@Temperature 73.0 °F
|
ASTM D256 |
| Gardner Impact | 1.36 J
@Temperature 22.8 °C
|
1.00 ft-lb
@Temperature 73.0 °F
|
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 47 % | 47 % | 60°; ASTM D523 |