Toyobo PELPRENE™ P40H Polyester TPE
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Features: Polyester TPE information provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.48 % | 0.48 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0050 cm/cm
@Thickness 2.00 mm
|
0.0050 in/in
@Thickness 0.0787 in
|
|
| Melt Index of Compound | 10 g/10 min
@Temperature 190 °C
|
10 g/10 min
@Temperature 374 °F
|
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 89 | 89 | JIS K6301 |
| Hardness, Shore D | 38 | 38 | ASTM D2240 |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 690 % | 690 % | ASTM D638 |
| 50% Modulus | 0.00640 GPa | 0.928 ksi | ASTM D638 |
| Flexural Modulus | 0.0510 GPa | 7.40 ksi | ASTM D790 |
| Compressive Modulus | 0.00450 GPa | 0.653 ksi | 0.1; ASTM D695 |
| Resilience | 78 | 78 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 98.0 kN/m | 559 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | ASTM D1044 |
| Compression Set | 50 % | 50 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C
@Temperature 20.0 °C
|
94.4 µin/in-°F
@Temperature 68.0 °F
|
TMA |
| Melting Point | 172 °C | 342 °F | By DSC |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+12 ohm-cm | 2.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | JIS K2111 |